The effect of thermal treatment of birch wood on the cutting power of plain milling

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41320%2F15%3A68534" target="_blank" >RIV/60460709:41320/15:68534 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.15376/biores.10.4.8528-8538" target="_blank" >http://dx.doi.org/10.15376/biores.10.4.8528-8538</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.15376/biores.10.4.8528-8538" target="_blank" >10.15376/biores.10.4.8528-8538</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of thermal treatment of birch wood on the cutting power of plain milling

Popis výsledku v původním jazyce

This article deals with cutting power during the plane milling of thermally treated and untreated silver birch (Betula pendula Roth.) wood. Thermal treatment was carried out at various temperatures of 160, 180, 210, and 240 °C. The cutting power was measured under various milling conditions, such as rake angle of tool (10°, 15°, 20°, 25°, and 30°), cutting speed (20, 40, and 60 m/s), and feed speed (4, 8, and 11 m/min). Thermal treatment had no clear impact on the cutting power. Treated wood at 160 and180 °C had lower values of cutting power in comparison with untreated wood, while the opposite trend was observed at 210 and 240 °C. The results show that with increasing speed feed, there is an increase in cutting power, while the opposite effect was achieved by changing the cutting speed. The optimum values of cutting power were achieved at a 10° angle and a thermal treatment of 160 °C.

Název v anglickém jazyce

The effect of thermal treatment of birch wood on the cutting power of plain milling

Popis výsledku anglicky

This article deals with cutting power during the plane milling of thermally treated and untreated silver birch (Betula pendula Roth.) wood. Thermal treatment was carried out at various temperatures of 160, 180, 210, and 240 °C. The cutting power was measured under various milling conditions, such as rake angle of tool (10°, 15°, 20°, 25°, and 30°), cutting speed (20, 40, and 60 m/s), and feed speed (4, 8, and 11 m/min). Thermal treatment had no clear impact on the cutting power. Treated wood at 160 and180 °C had lower values of cutting power in comparison with untreated wood, while the opposite trend was observed at 210 and 240 °C. The results show that with increasing speed feed, there is an increase in cutting power, while the opposite effect was achieved by changing the cutting speed. The optimum values of cutting power were achieved at a 10° angle and a thermal treatment of 160 °C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JP - Průmyslové procesy a zpracování

OECD FORD obor

—

Projekt

<a href="/cs/project/QJ1330233" target="_blank" >QJ1330233: Příprava legislativních, hospodářsko-úpravnických, mysliveckých a pěstitelsko-ochranářských rámců jako nástrojů adaptace lesního hospodářství na změny přírodních a společenských podmínek</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

BioResources

ISSN

1930-2126

e-ISSN

—

Svazek periodika

10

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

11

Strana od-do

8528-8538

Kód UT WoS článku

000366990800173

EID výsledku v databázi Scopus

—