Fire resistance of thermally modified Spruce wood

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41320%2F17%3A72276" target="_blank" >RIV/60460709:41320/17:72276 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.15376/biores.12.1.947-959" target="_blank" >http://dx.doi.org/10.15376/biores.12.1.947-959</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.15376/biores.12.1.947-959" target="_blank" >10.15376/biores.12.1.947-959</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fire resistance of thermally modified Spruce wood

Popis výsledku v původním jazyce

The risk of possible ignition and burning is one of the greatest disadvantages of using wood as a construction material. An environmentally appropriate method of improving the fire-resistant properties of wood is available via thermal treatment. In this study, spruce wood (Picea abies L.) was thermally modified at 160, 180 and 210 degrees Celsius. The effect of thermal modification on the fire performance of the wood, including weight loss and burn rate, was evaluated. A new testing method was designed to be sufficiently sensitive to monitor fire performance. The results showed that the thermally modified spruce wood had a lower weight loss than untreated wood. The burn rate of wood that was thermally modified at 160 degrees Celsius was similar to that of untreated wood. Higher thermal treatment temperatures caused a higher burn rate. After the flame was removed, the burning process was rapidly stopped in thermally treated wood.

Název v anglickém jazyce

Fire resistance of thermally modified Spruce wood

Popis výsledku anglicky

The risk of possible ignition and burning is one of the greatest disadvantages of using wood as a construction material. An environmentally appropriate method of improving the fire-resistant properties of wood is available via thermal treatment. In this study, spruce wood (Picea abies L.) was thermally modified at 160, 180 and 210 degrees Celsius. The effect of thermal modification on the fire performance of the wood, including weight loss and burn rate, was evaluated. A new testing method was designed to be sufficiently sensitive to monitor fire performance. The results showed that the thermally modified spruce wood had a lower weight loss than untreated wood. The burn rate of wood that was thermally modified at 160 degrees Celsius was similar to that of untreated wood. Higher thermal treatment temperatures caused a higher burn rate. After the flame was removed, the burning process was rapidly stopped in thermally treated wood.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20502 - Paper and wood

Projekt

<a href="/cs/project/QJ1330233" target="_blank" >QJ1330233: Příprava legislativních, hospodářsko-úpravnických, mysliveckých a pěstitelsko-ochranářských rámců jako nástrojů adaptace lesního hospodářství na změny přírodních a společenských podmínek</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

BioResources

ISSN

1930-2126

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

13

Strana od-do

947-959

Kód UT WoS článku

000397065200068

EID výsledku v databázi Scopus

—