Photoelectrochemical properties of particulate and sol-gel layers.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F03%3A00008339" target="_blank" >RIV/60461373:22310/03:00008339 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Photoelectrochemical properties of particulate and sol-gel layers.

Popis výsledku v původním jazyce

Polarization curves on irradiated TiO2 layers were measured in various electrolytes, namely sodium hydroxide, sulphuric acid, oxalic acid and potassium oxalate. Photocurrents measured in 0.1 M NaOH are very small and decrease with increasing number of Degussa P25 TiO2 layers. Photocurrents for sol-gel TiO2 layers in 0.1 M NaOH are about five times higher than for P25 TiO2 layers and increasing with number of layers. The same holds for Na2SO4, but in H2SO4 the difference between P25 and sol-gel diminishes, however the sol-gel layers still show the higher currents. In solutions of oxidizable substrates the trend is inversed: P25 layers show higher currents, with a steep increase with concentration of solute. The shape of the polarization curves was interpreted in terms of response time to irradiation and photocurrent depletion. Degradation experiments demonstrated that the effect (and advantage) of biasing the electrode depends on adsorption properties of substance and surface area of el

Název v anglickém jazyce

Photoelectrochemical properties of particulate and sol-gel layers.

Popis výsledku anglicky

Polarization curves on irradiated TiO2 layers were measured in various electrolytes, namely sodium hydroxide, sulphuric acid, oxalic acid and potassium oxalate. Photocurrents measured in 0.1 M NaOH are very small and decrease with increasing number of Degussa P25 TiO2 layers. Photocurrents for sol-gel TiO2 layers in 0.1 M NaOH are about five times higher than for P25 TiO2 layers and increasing with number of layers. The same holds for Na2SO4, but in H2SO4 the difference between P25 and sol-gel diminishes, however the sol-gel layers still show the higher currents. In solutions of oxidizable substrates the trend is inversed: P25 layers show higher currents, with a steep increase with concentration of solute. The shape of the polarization curves was interpreted in terms of response time to irradiation and photocurrent depletion. Degradation experiments demonstrated that the effect (and advantage) of biasing the electrode depends on adsorption properties of substance and surface area of el

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CG - Elektrochemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Photoenergy

ISSN

1110-662X

e-ISSN

—

Svazek periodika

5

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

EG - Egyptská arabská republika

Počet stran výsledku

7

Strana od-do

115-122

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—