Fotoelektrokatalytické vlastnosti TiO2 vrstev
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F05%3A00013703" target="_blank" >RIV/60461373:22310/05:00013703 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Photoelectrochemical properties of TiO2 layers
Popis výsledku v původním jazyce
Polarization curves on irradiated TiO2 layers were measured in various basic electrolytes, namely sodium hydroxide and sulphuric acid. Photocurrents for sol-gel TiO2 layers are in all mentioned electrolyte higher than that for Degussa P25 TiO2 layers. Insolutions of oxidizable substrates (oxalic acid) the trend is inversed: P25 layers show higher currents, with a steep increase with concentration of solute than at the TiO2 layer prepared by sol-gel. The effect of applied potential depends strongly on the type of TiO2 film. Photodegradation at open circuit is for particulate TiO2 film about 4 times higher than that for sol-gel film. Applying potential 0.6 V (SCE) on particulate film results in an increase about 130 % (in relation to open circuit degradation rate) while in the case of sol gel film the increase is much higher (about 350 %).
Název v anglickém jazyce
Photoelectrochemical properties of TiO2 layers
Popis výsledku anglicky
Polarization curves on irradiated TiO2 layers were measured in various basic electrolytes, namely sodium hydroxide and sulphuric acid. Photocurrents for sol-gel TiO2 layers are in all mentioned electrolyte higher than that for Degussa P25 TiO2 layers. Insolutions of oxidizable substrates (oxalic acid) the trend is inversed: P25 layers show higher currents, with a steep increase with concentration of solute than at the TiO2 layer prepared by sol-gel. The effect of applied potential depends strongly on the type of TiO2 film. Photodegradation at open circuit is for particulate TiO2 film about 4 times higher than that for sol-gel film. Applying potential 0.6 V (SCE) on particulate film results in an increase about 130 % (in relation to open circuit degradation rate) while in the case of sol gel film the increase is much higher (about 350 %).
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/1M0577" target="_blank" >1M0577: Výzkumné centrum pro nanopovrchové inženýrství</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2005
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Chemické listy
ISSN
0009-2770
e-ISSN
—
Svazek periodika
99
Číslo periodika v rámci svazku
S
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
2
Strana od-do
512-513
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—