Magnetizmus, transport a nábojové uspořádání v Bi1-xSrxMnO3

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F04%3A00011693" target="_blank" >RIV/60461373:22310/04:00011693 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Magnetism, transport and charge order in Bi1-xSrxMnO3

Popis výsledku v původním jazyce

The structural, magnetic and transport properties in the strontiumrich part of Bi$_{1-x}$Sr$_{x}$MnO$_{3}$ solid solution($xinlangle$0.5;1$rangle$) were examined by X-ray powderdiffraction, $DC$ susceptibility, thermopower, resisitivity andthermal conductivity measurements. All material characteristicsare significantly changed at the temperature of charge ordering,$T_{CO}$, which gradually decreases from $sim$~550 K for $x$=0.5to almost 0~K at $x$=0.9. Above $T_{CO}$ a temperature independentthermopower, whose absolute value increases with $x$, indicatespolaronic transport. Below $T_{CO}$ an activated transportmechanism of localized charge carriers is observed. The Weisstemperature decreases with $x$ and becomes negative for $x$=0.8suggesting antiferromagnetic interactions at high temperatures.The evolution of the above mentioned effects is accompanied by aprogressive decrease of orthorhombic distorsion at roomtemperature.

Název v anglickém jazyce

Magnetism, transport and charge order in Bi1-xSrxMnO3

Popis výsledku anglicky

The structural, magnetic and transport properties in the strontiumrich part of Bi$_{1-x}$Sr$_{x}$MnO$_{3}$ solid solution($xinlangle$0.5;1$rangle$) were examined by X-ray powderdiffraction, $DC$ susceptibility, thermopower, resisitivity andthermal conductivity measurements. All material characteristicsare significantly changed at the temperature of charge ordering,$T_{CO}$, which gradually decreases from $sim$~550 K for $x$=0.5to almost 0~K at $x$=0.9. Above $T_{CO}$ a temperature independentthermopower, whose absolute value increases with $x$, indicatespolaronic transport. Below $T_{CO}$ an activated transportmechanism of localized charge carriers is observed. The Weisstemperature decreases with $x$ and becomes negative for $x$=0.8suggesting antiferromagnetic interactions at high temperatures.The evolution of the above mentioned effects is accompanied by aprogressive decrease of orthorhombic distorsion at roomtemperature.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA203%2F03%2F0924" target="_blank" >GA203/03/0924: Efekty uspořádání a povaha chemické vazby v manganitech na bázi bizmutu</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Magnetism and Magnetic Materials

ISSN

0304-8853

e-ISSN

—

Svazek periodika

Neuveden

Číslo periodika v rámci svazku

272-276

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

2

Strana od-do

"e285"-"e286"

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—