Dielectric properties of doped polymethylmethacrylate

Popis výsledku v původním jazyce

Permittivity of about 1 #m thick films prepared from polymethylmetactrylate (PMMA) solution doped with 20% of diphenyl sulfoxide was studied. The film structure was characterized by XRD, RBS, DSC and SEM techniques. The dopant was found to be distributedhomogenously in the film volume. Permittivity of the films was measured as a function of the temperature. The measurement of the dependence of polarization on electrical field was performed using a standard Sawyer-Tower circuit. The presence of the dopant increases the composite permittivity namely above the PMMA glass transition temperature. Hysteresis loops observed on the measured polarization vs. electrical field dependence indicate easier and more pronounced polarizability of the composite comparing to pristine PMMA

Název v anglickém jazyce

Dielectric properties of doped polymethylmethacrylate

Popis výsledku anglicky

Permittivity of about 1 #m thick films prepared from polymethylmetactrylate (PMMA) solution doped with 20% of diphenyl sulfoxide was studied. The film structure was characterized by XRD, RBS, DSC and SEM techniques. The dopant was found to be distributedhomogenously in the film volume. Permittivity of the films was measured as a function of the temperature. The measurement of the dependence of polarization on electrical field was performed using a standard Sawyer-Tower circuit. The presence of the dopant increases the composite permittivity namely above the PMMA glass transition temperature. Hysteresis loops observed on the measured polarization vs. electrical field dependence indicate easier and more pronounced polarizability of the composite comparing to pristine PMMA

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA102%2F03%2F0449" target="_blank" >GA102/03/0449: Nové obvodové prvky pro sdělovací techniku</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Letters

ISSN

0167-577X

e-ISSN

—

Svazek periodika

59

Číslo periodika v rámci svazku

2-3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

341-344

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—