Sol gel multilayer TiO2 films, relation between crystallinity photoactivity and surface hydrophilicity

Popis výsledku v původním jazyce

This paper deals with the preparation and characterization of thin transparent films of TiO2 with particular interest to the effect of film thickness (repeated layer deposition) and to the relation between crystallinity, photoactivity and surface hydrophility. TiO2 layers were prepared by sol-gel method from titanium(IV) iso?propoxide, isopropyl alcohol and acetylacetone were used as solvents and hydrochloric acid as a catalyst. Final calcination was at 500 °C for 2 hours. Characterization was performedusing XRD, UV/VIS spectroscopy and SEM. Photoactivity was measured using two dyes: anionic acid orange 7 and cationic methylene blue.

Název v anglickém jazyce

Sol gel multilayer TiO2 films, relation between crystallinity photoactivity and surface hydrophilicity

Popis výsledku anglicky

This paper deals with the preparation and characterization of thin transparent films of TiO2 with particular interest to the effect of film thickness (repeated layer deposition) and to the relation between crystallinity, photoactivity and surface hydrophility. TiO2 layers were prepared by sol-gel method from titanium(IV) iso?propoxide, isopropyl alcohol and acetylacetone were used as solvents and hydrochloric acid as a catalyst. Final calcination was at 500 °C for 2 hours. Characterization was performedusing XRD, UV/VIS spectroscopy and SEM. Photoactivity was measured using two dyes: anionic acid orange 7 and cationic methylene blue.

Druh

D - Stať ve sborníku

CEP obor

CH - Jaderná a kvantová chemie, fotochemie

OECD FORD obor

—

Projekt

<a href="/cs/project/1M0577" target="_blank" >1M0577: Výzkumné centrum pro nanopovrchové inženýrství</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the workshop Recent advances in photochemistry, electrochemistry and photocatalysis

ISBN

978-80-7080-680-7

ISSN

—

e-ISSN

—

Počet stran výsledku

3

Strana od-do

—

Název nakladatele

VŠCHT Praha

Místo vydání

Praha

Místo konání akce

Hnanice

Datum konání akce

4. 12. 2007

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—