Plasma spraying of Fe-Cr-Al alloy powder

Popis výsledku v původním jazyce

The present paper deals with selective vaporization of Al and Cr from four binary alloy powders: Fe-Al, Fe-Cr, and Ni-Cr with two Cr concentration levels during the plasma spraying. The decrease of Al concentration in a Fe-Al alloy amounted to more than5 %, whereas the Cr concentration fall was not higher than 0.3% in Fe-Cr and Ni-Cr alloys. To interpret the experimental results, saturated vapor pressures of the important species were calculated as functions of temperature up to 3 200 K. For molten alloys, vaporization of elements was taken in consideration, whereas a wider variety of species evaporating from oxide melts was involved in the calculations. The results of thermodynamic calculations confirm the Cr concentration decrease in Fe-Cr and Ni-Cralloys. A lack of agreement relating to Al is most likely due to a different coverage of the molten Fe-Al alloy drop by Al-oxide melt.

Název v anglickém jazyce

Plasma spraying of Fe-Cr-Al alloy powder

Popis výsledku anglicky

The present paper deals with selective vaporization of Al and Cr from four binary alloy powders: Fe-Al, Fe-Cr, and Ni-Cr with two Cr concentration levels during the plasma spraying. The decrease of Al concentration in a Fe-Al alloy amounted to more than5 %, whereas the Cr concentration fall was not higher than 0.3% in Fe-Cr and Ni-Cr alloys. To interpret the experimental results, saturated vapor pressures of the important species were calculated as functions of temperature up to 3 200 K. For molten alloys, vaporization of elements was taken in consideration, whereas a wider variety of species evaporating from oxide melts was involved in the calculations. The results of thermodynamic calculations confirm the Cr concentration decrease in Fe-Cr and Ni-Cralloys. A lack of agreement relating to Al is most likely due to a different coverage of the molten Fe-Al alloy drop by Al-oxide melt.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA1041404" target="_blank" >IAA1041404: Atomové uspořádání u povrchů a rozhraní slitin 3d kovů.</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

46

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

9

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—