Odpařování složek z částic slitinových prášků v proudu plazmatu
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F06%3A00040309" target="_blank" >RIV/61389021:_____/06:00040309 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Vaporization of componets from alloy powder particles in a plasma flow
Popis výsledku v původním jazyce
During plasma spraying of alloy powders, their composition usually changes due to selective oxidation and selective vaporization. Selective vaporization of Al and Cr from four binary alloy powders (Fe-Al, Fe-Cr, and two Ni-Cr alloys) was studied. The decrease of Al concentration in a Fe-Al alloy amounted to more than 5%, whereas the Cr concentration fall was not higher than 0.3% in Fe-Cr and Ni-Cr alloys. The effect of selective oxidation was also quite different: Cr was consumed by oxidation at a considerably higher rate than Al. The interpretation of experimental results was based on equilibrium calculations of saturated vapour pressures of all important species at the temperatures up to 3200 K. The results of thermodynamic calculations confirm the Cr concentration decrease in Fe-Cr and Ni-Cr alloys. For Al, the agreement is not so good, which is due most likely to a different coverage of molten Fe-Al alloy drops by the Al-oxide melt.
Název v anglickém jazyce
Vaporization of componets from alloy powder particles in a plasma flow
Popis výsledku anglicky
During plasma spraying of alloy powders, their composition usually changes due to selective oxidation and selective vaporization. Selective vaporization of Al and Cr from four binary alloy powders (Fe-Al, Fe-Cr, and two Ni-Cr alloys) was studied. The decrease of Al concentration in a Fe-Al alloy amounted to more than 5%, whereas the Cr concentration fall was not higher than 0.3% in Fe-Cr and Ni-Cr alloys. The effect of selective oxidation was also quite different: Cr was consumed by oxidation at a considerably higher rate than Al. The interpretation of experimental results was based on equilibrium calculations of saturated vapour pressures of all important species at the temperatures up to 3200 K. The results of thermodynamic calculations confirm the Cr concentration decrease in Fe-Cr and Ni-Cr alloys. For Al, the agreement is not so good, which is due most likely to a different coverage of molten Fe-Al alloy drops by the Al-oxide melt.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F03%2F0710" target="_blank" >GA106/03/0710: Změny složení keramických a kovových materiálů při jejich plazmovém stříkání</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Czechoslovak Journal of Physics
ISSN
0011-4626
e-ISSN
—
Svazek periodika
56
Číslo periodika v rámci svazku
suppl.B
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
10
Strana od-do
"B1391"-"B1400"
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—