Using of electrochemical polarization method for detection of structural changes in heat-resistant steels after long-term creep exposition

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F12%3A43894743" target="_blank" >RIV/60461373:22310/12:43894743 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Using of electrochemical polarization method for detection of structural changes in heat-resistant steels after long-term creep exposition

Popis výsledku v původním jazyce

This work is focused on evaluation of structural changes in long-term creep stressed 9% Cr heat-resistant steel P92 using polarization method. Earlier studies showed that the shape of polarization curves of this steel in both sulphuric acid and sodium hydroxide solution slightly changes after long-term heating. This change is attributed to precipitation of phases enriched with elements easily soluble in transpassive region (chromium, molybdenum, tungsten). Moreover, transition into the transpassive region is active degradation process during oxidation in supercritical steam. The aim of this work is to assess the influence of exposition under different creep conditions. Scanning electron microscopy equipped with EDS analyser was used for structure observation and evaluation. Measured curves show very different electrochemical behaviour of heated and creep stressed steel. In addition, the influence of pure alloying elements was studied.

Název v anglickém jazyce

Using of electrochemical polarization method for detection of structural changes in heat-resistant steels after long-term creep exposition

Popis výsledku anglicky

This work is focused on evaluation of structural changes in long-term creep stressed 9% Cr heat-resistant steel P92 using polarization method. Earlier studies showed that the shape of polarization curves of this steel in both sulphuric acid and sodium hydroxide solution slightly changes after long-term heating. This change is attributed to precipitation of phases enriched with elements easily soluble in transpassive region (chromium, molybdenum, tungsten). Moreover, transition into the transpassive region is active degradation process during oxidation in supercritical steam. The aim of this work is to assess the influence of exposition under different creep conditions. Scanning electron microscopy equipped with EDS analyser was used for structure observation and evaluation. Measured curves show very different electrochemical behaviour of heated and creep stressed steel. In addition, the influence of pure alloying elements was studied.

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI1%2F086" target="_blank" >FR-TI1/086: Nové přístupy navrhování energetických zařízení a ocelových konstrukcí s vysokými užitnými parametry</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

New methods of damage and failure analysis of structural parts

ISBN

978-80-248-2802-2

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

473-479

Název nakladatele

VŠB - Technická univerzita

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

10. 9. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—