Structure and electrochemical behaviour of Fe-9Cr-W alloys with variable carbon and tungsten content
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F13%3A43896630" target="_blank" >RIV/60461373:22310/13:43896630 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structure and electrochemical behaviour of Fe-9Cr-W alloys with variable carbon and tungsten content
Popis výsledku v původním jazyce
Use of creep-resistant steel P92 in modern power plants enables increase of service temperature up to 650 °C. Some alloying elements (Cr, W) can easily increase their oxidation states and form volatile compounds in high steam parameters environments. Very similar degradation mechanism is observed in strongly oxidizing aqueous environments, where these alloys are subject to transpassive dissolution. Model melts containing constant chromium content (9 wt.%) and variable amount of carbon (0.01 - 0.63 wt. %) and tungsten (1.5 - 4.0 wt. %) were used for study of the influence of alloying elements. Structure of these alloys was characterized using optical and scanning electron microscope. Electrochemical behaviour was evaluated by potentiodynamic method. Model alloys showed to have dissimilar structure compared to industrial melts of P92, however, shapes of their potentiodynamic curves are very similar. The curve in transpassive area is accompanied by formation of substantial local peaks who
Název v anglickém jazyce
Structure and electrochemical behaviour of Fe-9Cr-W alloys with variable carbon and tungsten content
Popis výsledku anglicky
Use of creep-resistant steel P92 in modern power plants enables increase of service temperature up to 650 °C. Some alloying elements (Cr, W) can easily increase their oxidation states and form volatile compounds in high steam parameters environments. Very similar degradation mechanism is observed in strongly oxidizing aqueous environments, where these alloys are subject to transpassive dissolution. Model melts containing constant chromium content (9 wt.%) and variable amount of carbon (0.01 - 0.63 wt. %) and tungsten (1.5 - 4.0 wt. %) were used for study of the influence of alloying elements. Structure of these alloys was characterized using optical and scanning electron microscope. Electrochemical behaviour was evaluated by potentiodynamic method. Model alloys showed to have dissimilar structure compared to industrial melts of P92, however, shapes of their potentiodynamic curves are very similar. The curve in transpassive area is accompanied by formation of substantial local peaks who
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI1%2F086" target="_blank" >FR-TI1/086: Nové přístupy navrhování energetických zařízení a ocelových konstrukcí s vysokými užitnými parametry</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Conference METAL 2013 proceedings
ISBN
978-80-87294-39-0
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
817-821
Název nakladatele
Tanger, spol. s r.o.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
15. 5. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—