Formation of phases in Ti-Al system at 800 °C

Popis výsledku v původním jazyce

In this work, kinetics of the intermediary phase formation in Ti-Al system during reactive sintering at 800 °C was investigated. Because it is very difficult to determine the kinetics on the powder mixture, special model system was utilized. This model consisted of solid titanium and molten aluminium and the intermediary phase formation was observed on the interface solid - liquid state at various times. Only TiAl3 phase formed during the test. The thickness of the layer was changing and based on these results it can be estimated how the process is controlled. It was revealed that the formation of TiAl3 phase is controlled by the rate of chemical reaction and the incubation period is 5 and 75 min.

Název v anglickém jazyce

Formation of phases in Ti-Al system at 800 °C

Popis výsledku anglicky

In this work, kinetics of the intermediary phase formation in Ti-Al system during reactive sintering at 800 °C was investigated. Because it is very difficult to determine the kinetics on the powder mixture, special model system was utilized. This model consisted of solid titanium and molten aluminium and the intermediary phase formation was observed on the interface solid - liquid state at various times. Only TiAl3 phase formed during the test. The thickness of the layer was changing and based on these results it can be estimated how the process is controlled. It was revealed that the formation of TiAl3 phase is controlled by the rate of chemical reaction and the incubation period is 5 and 75 min.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

17

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

5

Strana od-do

838-842

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85030528088