Corrosion behaviour of the titanium beta alloy nanotubular surface in the presence of fluoride ions

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F19%3A43919582" target="_blank" >RIV/60461373:22310/19:43919582 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.2478/kom-2019-0009" target="_blank" >https://doi.org/10.2478/kom-2019-0009</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.2478/kom-2019-0009" target="_blank" >10.2478/kom-2019-0009</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Corrosion behaviour of the titanium beta alloy nanotubular surface in the presence of fluoride ions

Popis výsledku v původním jazyce

The titanium bioactivity could be increased by surface nanostructuring. Titanium alloys are using for dental implants manufacturing. It represents a specific problem because of using of the dental treatments with high concentration of fluoride ions and with acidic pH. The corrosion resistance of nanostructured surface of titanium beta alloy in environments with fluoride ions was examined by common electrochemical technique. The electrochemical impedance measurement showed high corrosion resistance in physiological solution. The fluoride ions have expected negative influence on corrosion behaviour of the layer. The nanotube bottom was preferentially attacked which resulted in layer undercoroding and its detachment.

Název v anglickém jazyce

Corrosion behaviour of the titanium beta alloy nanotubular surface in the presence of fluoride ions

Popis výsledku anglicky

The titanium bioactivity could be increased by surface nanostructuring. Titanium alloys are using for dental implants manufacturing. It represents a specific problem because of using of the dental treatments with high concentration of fluoride ions and with acidic pH. The corrosion resistance of nanostructured surface of titanium beta alloy in environments with fluoride ions was examined by common electrochemical technique. The electrochemical impedance measurement showed high corrosion resistance in physiological solution. The fluoride ions have expected negative influence on corrosion behaviour of the layer. The nanotube bottom was preferentially attacked which resulted in layer undercoroding and its detachment.

Druh

J_ost - Ostatní články v recenzovaných periodicích

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA16-14758S" target="_blank" >GA16-14758S: Vliv nanotopografie povrchu na bioaktivní vlastnosti titanové slitiny s nízkým modulem pružnosti.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Koroze a ochrana materiálu

ISSN

0452-599X

e-ISSN

—

Svazek periodika

63

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

72-78

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—