Novel aircraft Mg-Y-Gd-Ca alloys with high ignition temperature and suppressed flammability

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F20%3A43920862" target="_blank" >RIV/60461373:22310/20:43920862 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/20:10423778

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0167577X20300185?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0167577X20300185?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matlet.2020.127313" target="_blank" >10.1016/j.matlet.2020.127313</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Novel aircraft Mg-Y-Gd-Ca alloys with high ignition temperature and suppressed flammability

Popis výsledku v původním jazyce

The ban by the Federal Aviation Administration (FAA) of application of magnesium in aircraft cabins was lifted under the condition that the used materials have to fulfill the requirements for the ignition tests. This work proposes the novel Mg-2Y-2Gd-1Ca alloy with a small amount of Y, Gd and Ca as main alloying elements. Superior ignition temperature of 1100 °C was determined for this alloy. Analysis of the oxide layers revealed the presence of Y2O3, CaO, Gd2O3, and MgO in oxide layers which were observed to significantly suppress ignition compared to the pure Mg. © 2020 Elsevier B.V.

Název v anglickém jazyce

Novel aircraft Mg-Y-Gd-Ca alloys with high ignition temperature and suppressed flammability

Popis výsledku anglicky

The ban by the Federal Aviation Administration (FAA) of application of magnesium in aircraft cabins was lifted under the condition that the used materials have to fulfill the requirements for the ignition tests. This work proposes the novel Mg-2Y-2Gd-1Ca alloy with a small amount of Y, Gd and Ca as main alloying elements. Superior ignition temperature of 1100 °C was determined for this alloy. Analysis of the oxide layers revealed the presence of Y2O3, CaO, Gd2O3, and MgO in oxide layers which were observed to significantly suppress ignition compared to the pure Mg. © 2020 Elsevier B.V.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA19-08937S" target="_blank" >GA19-08937S: Pokročilé slitiny hořčíku s potlačenou hořlavostí, vysokou korozní odolností a vysokou pevností</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Letters

ISSN

0167-577X

e-ISSN

—

Svazek periodika

264

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85077647147