Creation of Gold Nanoparticles in ZnO by Ion Implantation-DFT and Experimental Studies

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F20%3A43921021" target="_blank" >RIV/60461373:22310/20:43921021 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61389005:_____/20:00538371 RIV/44555601:13440/20:43896033

Výsledek na webu

<a href="https://www.mdpi.com/2079-4991/10/12/2392" target="_blank" >https://www.mdpi.com/2079-4991/10/12/2392</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/nano10122392" target="_blank" >10.3390/nano10122392</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Creation of Gold Nanoparticles in ZnO by Ion Implantation-DFT and Experimental Studies

Popis výsledku v původním jazyce

Three different crystallographic orientations of the wurtzite ZnO structure (labeled as c-plane, a-plane and m-plane) were implanted with Au+ ions using various energies and fluences to form gold nanoparticles (GNPs). The ion implantation process was followed by annealing at 600 degrees C in an oxygen atmosphere to decrease the number of unwanted defects and improve luminescence properties. With regard to our previous publications, the paper provides a summary of theoretical and experimental results, i.e., both DFT and FLUX simulations, as well as experimental results from TEM, HRTEM, RBS, RBS/C, Raman spectroscopy and photoluminescence. From the results, it follows that in the ZnO structure, implanted gold atoms are located in random interstitial positions -experimentally, the amount of interstitial gold atoms increased with increasing ion implantation fluence. During ion implantation and subsequent annealing, the metal clusters and nanoparticles with sizes from 2 to 20 nm were formed. The crystal structure of the resulting gold was not cubic (confirmed by diffraction patterns), but it had a hexagonal close-packed (hcp) arrangement. The ion implantation of gold leads to the creation of Zn and O interstitial defects and extended defects with distinct character in various crystallographic cuts of ZnO, where significant O-sublattice disordering occurred in m-plane ZnO.

Název v anglickém jazyce

Creation of Gold Nanoparticles in ZnO by Ion Implantation-DFT and Experimental Studies

Popis výsledku anglicky

Three different crystallographic orientations of the wurtzite ZnO structure (labeled as c-plane, a-plane and m-plane) were implanted with Au+ ions using various energies and fluences to form gold nanoparticles (GNPs). The ion implantation process was followed by annealing at 600 degrees C in an oxygen atmosphere to decrease the number of unwanted defects and improve luminescence properties. With regard to our previous publications, the paper provides a summary of theoretical and experimental results, i.e., both DFT and FLUX simulations, as well as experimental results from TEM, HRTEM, RBS, RBS/C, Raman spectroscopy and photoluminescence. From the results, it follows that in the ZnO structure, implanted gold atoms are located in random interstitial positions -experimentally, the amount of interstitial gold atoms increased with increasing ion implantation fluence. During ion implantation and subsequent annealing, the metal clusters and nanoparticles with sizes from 2 to 20 nm were formed. The crystal structure of the resulting gold was not cubic (confirmed by diffraction patterns), but it had a hexagonal close-packed (hcp) arrangement. The ion implantation of gold leads to the creation of Zn and O interstitial defects and extended defects with distinct character in various crystallographic cuts of ZnO, where significant O-sublattice disordering occurred in m-plane ZnO.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

21001 - Nano-materials (production and properties)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nanomaterials

ISSN

2079-4991

e-ISSN

—

Svazek periodika

10

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

21

Strana od-do

—

Kód UT WoS článku

000603115000001

EID výsledku v databázi Scopus

2-s2.0-85097097866