Localized corrosion attack on the galvanised steel pipes of the fire protection system
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F24%3A43931223" target="_blank" >RIV/60461373:22310/24:43931223 - isvavai.cz</a>
Výsledek na webu
<a href="https://sciendo.com/article/10.2478/kom-2024-0004" target="_blank" >https://sciendo.com/article/10.2478/kom-2024-0004</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.2478/kom-2024-0004" target="_blank" >10.2478/kom-2024-0004</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Localized corrosion attack on the galvanised steel pipes of the fire protection system
Popis výsledku v původním jazyce
Galvanised steel serves as a base material for pipelines in fire protection systems. However, this system is known for its occasional corrosion failures. The Systems with residual water and oxygen access contribute to formation of macrocells due to different aeration, which can lead to severe damage of the pipes. The aim of this work was to investigate the cause of localized corrosion on the galvanised pipes designated for the fire protection system. The results proved that the main cause of the fire protection pipe system was the residual water in the pipe. The influence of differential aeration on the corrosion of zinc and steel was studied by resistometric technique and showed no effect on the failure of material. © 2024 Sciendo. All rights reserved.
Název v anglickém jazyce
Localized corrosion attack on the galvanised steel pipes of the fire protection system
Popis výsledku anglicky
Galvanised steel serves as a base material for pipelines in fire protection systems. However, this system is known for its occasional corrosion failures. The Systems with residual water and oxygen access contribute to formation of macrocells due to different aeration, which can lead to severe damage of the pipes. The aim of this work was to investigate the cause of localized corrosion on the galvanised pipes designated for the fire protection system. The results proved that the main cause of the fire protection pipe system was the residual water in the pipe. The influence of differential aeration on the corrosion of zinc and steel was studied by resistometric technique and showed no effect on the failure of material. © 2024 Sciendo. All rights reserved.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2024
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Koroze a Ochrana Materialu
ISSN
0452-599X
e-ISSN
—
Svazek periodika
68
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
15
Strana od-do
28-42
Kód UT WoS článku
—
EID výsledku v databázi Scopus
2-s2.0-85190496988