Polykrystalické vrstvy silikalitu-1: textura a kinetika růstu

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F05%3A00000609" target="_blank" >RIV/61388955:_____/05:00000609 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Polycrystalline silicalite-1 layers: texture and kinetics of growth

Popis výsledku v původním jazyce

Self-supporting silicalite-1 layers were grown on mercury surface from clear solutions at temperatures 140-180oC. Synthesis time was varied. Kinetics of layer growth was measured and the corresponding apparent activation energy was estimated to 52kJ/mol.Layer morphology and thickness were characterized by SEM. Phase purity of silicalite-1 and orientation of crystals were determined by XRD. Density measurements of polycrystalline layers were carried out by helium pycnometry and by hydrostatic method. Layers with the thickness >40.mu.m were found to be highly compact. Relevancy of Brownian motion of colloidal particles besides their sedimentation is shown.

Název v anglickém jazyce

Polycrystalline silicalite-1 layers: texture and kinetics of growth

Popis výsledku anglicky

Self-supporting silicalite-1 layers were grown on mercury surface from clear solutions at temperatures 140-180oC. Synthesis time was varied. Kinetics of layer growth was measured and the corresponding apparent activation energy was estimated to 52kJ/mol.Layer morphology and thickness were characterized by SEM. Phase purity of silicalite-1 and orientation of crystals were determined by XRD. Density measurements of polycrystalline layers were carried out by helium pycnometry and by hydrostatic method. Layers with the thickness >40.mu.m were found to be highly compact. Relevancy of Brownian motion of colloidal particles besides their sedimentation is shown.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Microporous and Mesoporous Materials

ISSN

1387-1811

e-ISSN

—

Svazek periodika

78

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

29-36

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—