Vysoce porézní filmy films z anodicky deponovaných titanátových hybridů a jejich fotoelektrochemická a fotokatalytická aktivita

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F08%3A00309561" target="_blank" >RIV/61388955:_____/08:00309561 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Highly porous TiO2 films from anodically deposited titanate hybrids and their photoelectrochemical and photocatalytic activity

Popis výsledku v původním jazyce

Hybrid films of TiO2 and benzoquinone, its derivative 2-methyl-benzoquinone or the dye 2,9,16,23-tetrasulfophthalocyaninatonickel(II) were prepared by anodic electrodeposition from titanium alkoxide solutions. Calcination of the films at 450 degrees C led to removal of the organics and the formation of crystalline and highly porous TiO2 films as seen in XRD and Kr adsorption measurements, respectively. In dye-sensitized solar cells the films achieved an overall light-to-electricity conversion efficiencyof 0.8% despite a low film thickness of 0.55 mu m. In the photocatalytic decomposition of methylene blue the films showed photonic efficiencies of up to 0.09% for film thicknesses around 0.5 mu m, which is much higher than those of comparable TiO2 filmsprepared by sol-gel method.

Název v anglickém jazyce

Highly porous TiO2 films from anodically deposited titanate hybrids and their photoelectrochemical and photocatalytic activity

Popis výsledku anglicky

Hybrid films of TiO2 and benzoquinone, its derivative 2-methyl-benzoquinone or the dye 2,9,16,23-tetrasulfophthalocyaninatonickel(II) were prepared by anodic electrodeposition from titanium alkoxide solutions. Calcination of the films at 450 degrees C led to removal of the organics and the formation of crystalline and highly porous TiO2 films as seen in XRD and Kr adsorption measurements, respectively. In dye-sensitized solar cells the films achieved an overall light-to-electricity conversion efficiencyof 0.8% despite a low film thickness of 0.55 mu m. In the photocatalytic decomposition of methylene blue the films showed photonic efficiencies of up to 0.09% for film thicknesses around 0.5 mu m, which is much higher than those of comparable TiO2 filmsprepared by sol-gel method.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/1M0577" target="_blank" >1M0577: Výzkumné centrum pro nanopovrchové inženýrství</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Microporous and Mesoporous Materials

ISSN

1387-1811

e-ISSN

—

Svazek periodika

111

Číslo periodika v rámci svazku

1-3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

255847100010

EID výsledku v databázi Scopus

—