Organized Mesoporous TiO2 Films Stabilized by Phosphorus: Application for Dye-Sensitized Solar Cells

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F10%3A00331908" target="_blank" >RIV/61388955:_____/10:00331908 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Organized Mesoporous TiO2 Films Stabilized by Phosphorus: Application for Dye-Sensitized Solar Cells

Popis výsledku v původním jazyce

A synthetic protocol was developed for the preparation of thin mesoporous TiO2 films with enhanced thermal stability. This objective was achieved by a modification of the procedure of supramolecular templating by a Pluronic P-123 copolymer by an additionof a small amount of phosphoric acid to the precursor solution. Thin mesoporous TiO2 films up to 2.3 ?m thick were prepared via layer-by-layer deposition. The roughness factor exceeding 1300 was achieved on these films. After annealing at 540°C, well-developed 5?6 nm anatase nanocrystals were present in the pore walls of a still perfect mesoporous structure. The pore coalescence and structure collapse during heat-treatment were effectively hindered by the presence of phosphorus. Our P-modified mesoporous TiO2 films were sensitized with the N-945 dye and used as photoanodes of the dye-sensitized solar cells. They reached the conversion efficiency of 5.03 or 5.05% for the film thickness of 1.8 or 2.3 ?m, respectively.

Název v anglickém jazyce

Organized Mesoporous TiO2 Films Stabilized by Phosphorus: Application for Dye-Sensitized Solar Cells

Popis výsledku anglicky

A synthetic protocol was developed for the preparation of thin mesoporous TiO2 films with enhanced thermal stability. This objective was achieved by a modification of the procedure of supramolecular templating by a Pluronic P-123 copolymer by an additionof a small amount of phosphoric acid to the precursor solution. Thin mesoporous TiO2 films up to 2.3 ?m thick were prepared via layer-by-layer deposition. The roughness factor exceeding 1300 was achieved on these films. After annealing at 540°C, well-developed 5?6 nm anatase nanocrystals were present in the pore walls of a still perfect mesoporous structure. The pore coalescence and structure collapse during heat-treatment were effectively hindered by the presence of phosphorus. Our P-modified mesoporous TiO2 films were sensitized with the N-945 dye and used as photoanodes of the dye-sensitized solar cells. They reached the conversion efficiency of 5.03 or 5.05% for the film thickness of 1.8 or 2.3 ?m, respectively.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CG - Elektrochemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the Electrochemical Society

ISSN

0013-4651

e-ISSN

—

Svazek periodika

157

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000272387200094

EID výsledku v databázi Scopus

—