Highly conducting nanosized monodispersed antimony-doped tin oxide particles synthesized via nanoaqueous sol-gel method

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F10%3A00346542" target="_blank" >RIV/61388955:_____/10:00346542 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Highly conducting nanosized monodispersed antimony-doped tin oxide particles synthesized via nanoaqueous sol-gel method

Popis výsledku v původním jazyce

Conducting antimony-doped tin oxide (ATO) nanoparticles were prepared by a nonaqueous solution route, using benzyl alcohol as both the oxygen source and the solvent, and tin tetrachloride and Sb(III)/Sb(V) compounds as tin and antimony, respectively. This reaction produced non-agglomerated crystalline particles 3-4 nm in size, which can be easily redispersed in high concentrations in a variety of solvents to form stable transparent colloidal solutions without any stabilizing agents. The introduction ofSb dopant dramatically increased the particle conductivity, which reaches a maximum of 1.10(-4)S cm(-1) for 4% of Sb. Annealing in air at 500oC further improves the conductivity to 2.10(2)S cm(-1).

Název v anglickém jazyce

Highly conducting nanosized monodispersed antimony-doped tin oxide particles synthesized via nanoaqueous sol-gel method

Popis výsledku anglicky

Conducting antimony-doped tin oxide (ATO) nanoparticles were prepared by a nonaqueous solution route, using benzyl alcohol as both the oxygen source and the solvent, and tin tetrachloride and Sb(III)/Sb(V) compounds as tin and antimony, respectively. This reaction produced non-agglomerated crystalline particles 3-4 nm in size, which can be easily redispersed in high concentrations in a variety of solvents to form stable transparent colloidal solutions without any stabilizing agents. The introduction ofSb dopant dramatically increased the particle conductivity, which reaches a maximum of 1.10(-4)S cm(-1) for 4% of Sb. Annealing in air at 500oC further improves the conductivity to 2.10(2)S cm(-1).

Druh

C - Kapitola v odborné knize

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F08%2F0435" target="_blank" >GA104/08/0435: "Inteligentně strukturované" mesoporézní vrstvy TiO2 s antibakteriálními a řízeně proměnnými smáčecími vlastnostmi</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Nanotechnology 2010: Advanced Materials, CNTs, Particles, Films and Composites

ISBN

978-1-4398-3401-5

Počet stran výsledku

4

Strana od-do

—

Počet stran knihy

976

Název nakladatele

Taylor-Francis

Místo vydání

Boca Raton

Kód UT WoS kapitoly

—