Glass formation in the PbCl2-Sb2O3-TeO2 system.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F03%3A50033004" target="_blank" >RIV/61388980:_____/03:50033004 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Glass formation in the PbCl2-Sb2O3-TeO2 system.

Popis výsledku v původním jazyce

The aim of this work is the investigation of glass forming ability in the system of PbCl2 (PbO), Sb2O3 and TeO2 and the study of chemical and physical properties of found glasses. The investigation of physical properties was focused on thermal properties(glass transition temperature T-g, crystallization temperature T-x, thermal stability, thermal expansion coefficient CTE, etc.) and optical properties (especially optical transmissivity in visible and infrared region of spectra). Glass preparation is carried out in silica crucibles at room atmosphere, using chemically pure (>99.9%) reagents. Glass samples were obtained by quenching of the melt in case of less stable compositions or by casting in metal moulds in case of bulks. The glasses in the PbCl2-Sb2O3-TeO2 system are transparent from approximately 400 nm up to 6 microns and their T-g is about 200-300degreesC in dependence on glass composition.

Název v anglickém jazyce

Glass formation in the PbCl2-Sb2O3-TeO2 system.

Popis výsledku anglicky

The aim of this work is the investigation of glass forming ability in the system of PbCl2 (PbO), Sb2O3 and TeO2 and the study of chemical and physical properties of found glasses. The investigation of physical properties was focused on thermal properties(glass transition temperature T-g, crystallization temperature T-x, thermal stability, thermal expansion coefficient CTE, etc.) and optical properties (especially optical transmissivity in visible and infrared region of spectra). Glass preparation is carried out in silica crucibles at room atmosphere, using chemically pure (>99.9%) reagents. Glass samples were obtained by quenching of the melt in case of less stable compositions or by casting in metal moulds in case of bulks. The glasses in the PbCl2-Sb2O3-TeO2 system are transparent from approximately 400 nm up to 6 microns and their T-g is about 200-300degreesC in dependence on glass composition.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F02%2F0799" target="_blank" >GA104/02/0799: Speciální skla pro optoelektroniku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Solid State Phenomena

ISSN

1012-0394

e-ISSN

—

Svazek periodika

90-91

Číslo periodika v rámci svazku

N/A

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

235-240

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—