Electrical and optical properties of glasses based on TeO2-Sb2O3-PbCl2

Popis výsledku v původním jazyce

There were investigated optical transmittance and direct electrical conductivity of the g lass systems of TeO2-Sb2O3-PbCl2. Optical transmittance measured in the wave range of (2.5-7.5) mu m depends significantly on the amount and the nature of defects of glasses and the glass composition. The highest value of optical transmittance was found for glass of the composition of 40 TeO2 - 10 Sb2O3 - 50PbCl(2). Direct electrical conductivity in the temperature range of (20 - 240) degrees C has the constant value of activation energy (similar to 1.1 eV) if glasses own the low concentration of PbCl2. If the concentration of PbCl2 is increased then the change of value of activation energy at the temperature - 80 degrees C was observed. The values of conductivityof the system TeO2-Sb2O3-PbCl2 are strongly affected by the concentration of PbCl2.

Název v anglickém jazyce

Electrical and optical properties of glasses based on TeO2-Sb2O3-PbCl2

Popis výsledku anglicky

There were investigated optical transmittance and direct electrical conductivity of the g lass systems of TeO2-Sb2O3-PbCl2. Optical transmittance measured in the wave range of (2.5-7.5) mu m depends significantly on the amount and the nature of defects of glasses and the glass composition. The highest value of optical transmittance was found for glass of the composition of 40 TeO2 - 10 Sb2O3 - 50PbCl(2). Direct electrical conductivity in the temperature range of (20 - 240) degrees C has the constant value of activation energy (similar to 1.1 eV) if glasses own the low concentration of PbCl2. If the concentration of PbCl2 is increased then the change of value of activation energy at the temperature - 80 degrees C was observed. The values of conductivityof the system TeO2-Sb2O3-PbCl2 are strongly affected by the concentration of PbCl2.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Optoelectronics and Advanced Materials

ISSN

1454-4164

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

RO - Rumunsko

Počet stran výsledku

4

Strana od-do

1683-1686

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—