Preparation of CuFe2O4/SiO2 nanocomposite by the sol-gel method
Popis výsledku v původním jazyce
This work aims at characterizing the phase relations in the CuFe2O4/SiO2 system. Samples were prepared by the sol-gel method. Final heat treatment of the samples was carried out at temperatures in the range of 800-1100 degrees C. Final products were characterized by HR TEM, X-ray diffraction, magnetic measurements, and Mossbauer spectroscopy. HR TEM revealed nanocrystals with sizes of 7-130 nm, depending on the heat treatment temperature. The spinel structure of CuFe2O4 in the amorphous silica matrix proved to be stable up to 1100 degrees C without decomposition to copper silicate and iron (III) oxide. At the same time, the amorphous silica matrix recrystallized to cristobalite at 1100 degrees C.
Název v anglickém jazyce
Preparation of CuFe2O4/SiO2 nanocomposite by the sol-gel method
Popis výsledku anglicky
This work aims at characterizing the phase relations in the CuFe2O4/SiO2 system. Samples were prepared by the sol-gel method. Final heat treatment of the samples was carried out at temperatures in the range of 800-1100 degrees C. Final products were characterized by HR TEM, X-ray diffraction, magnetic measurements, and Mossbauer spectroscopy. HR TEM revealed nanocrystals with sizes of 7-130 nm, depending on the heat treatment temperature. The spinel structure of CuFe2O4 in the amorphous silica matrix proved to be stable up to 1100 degrees C without decomposition to copper silicate and iron (III) oxide. At the same time, the amorphous silica matrix recrystallized to cristobalite at 1100 degrees C.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2005
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science - Poland
ISSN
0137-1339
e-ISSN
—
Svazek periodika
23
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
9
Strana od-do
697-705
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—