Transformace brookituTiO2 nanokrystalů na rutil TiO2: korelce mezi mikrostrukturou a fotoaktivitou
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F06%3A00050332" target="_blank" >RIV/61388980:_____/06:00050332 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11310/06:12575
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Transformation of brookite-type TiO2 nanocrystals to rutile: correlation between microstructure and photoactivity
Popis výsledku v původním jazyce
Nanometric particles of pure brookite TiO2 were synthesized by modified thermolysis of reactant solutions containing titania powder, HCl, urea and PEG 10000. Unique flower-like brookite agglomerates with an average diameter of similar to 400-450 nm composed of single brookite nanocrystals of similar to 4-5 nm were obtained at 105 degrees C. The brookite -> rutile transformation has been studied and TiO2 mixtures with variable amount of anatase, brookite and rutile polymorphs at different temperatures (from 200 to 800 degrees C) were obtained. High resolution transmission electron microscopy (HRTEM), electron diffraction pattern and BET/BJH analyses were used to characterize the phase assemblages, crystallite size and pore volume of the pure-phase brookite and TiO2 mixtures. In order to understand the metastable-stable TiO2 phase transformation X-ray powder diffraction (XRD) was performed.
Název v anglickém jazyce
Transformation of brookite-type TiO2 nanocrystals to rutile: correlation between microstructure and photoactivity
Popis výsledku anglicky
Nanometric particles of pure brookite TiO2 were synthesized by modified thermolysis of reactant solutions containing titania powder, HCl, urea and PEG 10000. Unique flower-like brookite agglomerates with an average diameter of similar to 400-450 nm composed of single brookite nanocrystals of similar to 4-5 nm were obtained at 105 degrees C. The brookite -> rutile transformation has been studied and TiO2 mixtures with variable amount of anatase, brookite and rutile polymorphs at different temperatures (from 200 to 800 degrees C) were obtained. High resolution transmission electron microscopy (HRTEM), electron diffraction pattern and BET/BJH analyses were used to characterize the phase assemblages, crystallite size and pore volume of the pure-phase brookite and TiO2 mixtures. In order to understand the metastable-stable TiO2 phase transformation X-ray powder diffraction (XRD) was performed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Materials Chemistry
ISSN
0959-9428
e-ISSN
—
Svazek periodika
16
Číslo periodika v rámci svazku
18
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
1709-1716
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—