Devitrification kinetics of Sb2O3-PbI2 glasses

Popis výsledku v původním jazyce

Devitrification kinetics of Sb2O3-PbI2 glasses. Devitrification of oxyhalide glasses in the (1-x)Sb2O3-xPbI(2) system has been investigated by Differential Scanning Calorimetry (DSC). A single exotherm is observed in the DSC scan beyond the glass transition temperature Tg, which ensures the applicability of the Mehl-Johnson-Avrami-Kolmogorov relations. Non-isothermal measurements give access to the values of Avrami exponent n and activation energy E. E lies between 300 to 600kJ/mol and increases as leadiodide content increases. Exponent n also increases with PbI2 concentration: it ranges from 2.8 to 3.8. These results are consistent with the stability factors based on characteristic temperatures and confirm that the 90% Sb2O3 glass is the most stable.Crystal growth mechanism is discussed in relation to SEM observations.

Název v anglickém jazyce

Devitrification kinetics of Sb2O3-PbI2 glasses

Popis výsledku anglicky

Devitrification kinetics of Sb2O3-PbI2 glasses. Devitrification of oxyhalide glasses in the (1-x)Sb2O3-xPbI(2) system has been investigated by Differential Scanning Calorimetry (DSC). A single exotherm is observed in the DSC scan beyond the glass transition temperature Tg, which ensures the applicability of the Mehl-Johnson-Avrami-Kolmogorov relations. Non-isothermal measurements give access to the values of Avrami exponent n and activation energy E. E lies between 300 to 600kJ/mol and increases as leadiodide content increases. Exponent n also increases with PbI2 concentration: it ranges from 2.8 to 3.8. These results are consistent with the stability factors based on characteristic temperatures and confirm that the 90% Sb2O3 glass is the most stable.Crystal growth mechanism is discussed in relation to SEM observations.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Annales de Chimie-Science Des Materiaux

ISSN

0151-9107

e-ISSN

—

Svazek periodika

34

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

FR - Francouzská republika

Počet stran výsledku

18

Strana od-do

—

Kód UT WoS článku

000272642200005

EID výsledku v databázi Scopus

—