Stress analysis of the hip joint endoprosthesis ceramic head for different values of shape deviations

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388998%3A_____%2F14%3A00441585" target="_blank" >RIV/61388998:_____/14:00441585 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.936.770" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMR.936.770</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.936.770" target="_blank" >10.4028/www.scientific.net/AMR.936.770</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Stress analysis of the hip joint endoprosthesis ceramic head for different values of shape deviations

Popis výsledku v původním jazyce

The paper deals with the problems of ceramic head of hip joint endoprosthesis destructions, and with assessing the impact of shape deviations of conical surfaces on the tensile stress under ISO 7206-5 loading. The failure of the hip joint endoprosthesisceramic head has always traumatic consequences for the patient, since a part of or even the whole endoprosthesis has to be reoperated. Hence, it is desired to reduce the number of implant re-operations to the minimum. Therefore the computational modelling of the stress of the head was realised. The shape deviations of the ideal contact cone areas of the head and stem are parameters that significantly influence the tensile stress in the head and its reliability. The assumed shape deviations of the head'sand stem's cones are macro shape deviations (different cone taper) and micro shape deviations (unevennes) measured using the IMS-UMPIRE equipment. The stress state in the ceramic heads was solved using the FEM and head's failure probabil

Název v anglickém jazyce

Stress analysis of the hip joint endoprosthesis ceramic head for different values of shape deviations

Popis výsledku anglicky

The paper deals with the problems of ceramic head of hip joint endoprosthesis destructions, and with assessing the impact of shape deviations of conical surfaces on the tensile stress under ISO 7206-5 loading. The failure of the hip joint endoprosthesisceramic head has always traumatic consequences for the patient, since a part of or even the whole endoprosthesis has to be reoperated. Hence, it is desired to reduce the number of implant re-operations to the minimum. Therefore the computational modelling of the stress of the head was realised. The shape deviations of the ideal contact cone areas of the head and stem are parameters that significantly influence the tensile stress in the head and its reliability. The assumed shape deviations of the head'sand stem's cones are macro shape deviations (different cone taper) and micro shape deviations (unevennes) measured using the IMS-UMPIRE equipment. The stress state in the ceramic heads was solved using the FEM and head's failure probabil

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA13-34632S" target="_blank" >GA13-34632S: Zvýšení úrovně výpočtového modelování chování keramické hlavice totální kyčelní endoprotézy</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Advanced Materials Research

ISBN

978-3-03835-102-3

ISSN

1022-6680

e-ISSN

—

Počet stran výsledku

6

Strana od-do

770-775

Název nakladatele

Trans Tech Publications Ltd

Místo vydání

Dürnten

Místo konání akce

Shanghai

Datum konání akce

28. 6. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—