Compositional alteration of polyimide under high fluence implantation by Co+ and Fe+ ions.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F03%3A49033095" target="_blank" >RIV/61389005:_____/03:49033095 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Compositional alteration of polyimide under high fluence implantation by Co+ and Fe+ ions.
Popis výsledku v původním jazyce
Polyimide(PI) foils were implanted with 40 keV Fe+ and Co+ ions to the fluences of 2.5 x 10(16)-1.25 x 10(17) cm(-2) at the ion current densities of 4, 8 and 12 muA cm(-2). Surface morphology and compositional alteration of the implanted polymer have been studied using atomic force microscopy, transmission electron microscopy, Rutherford backscattering and X-ray photoelectron spectroscopy. Carbonisation of the surface layer, followed by oxygen and nitrogen depletion is observed. These processes reach the saturation level at the applied high fluences. A further increase of ion fluence and density of ion current does not change the composition; only an increase in the metal concentration is observed. It is shown that metal ion implantation to high fluence at high ion current density can be effectively employed to form metal/polymer nanocomposites with required parameters.
Název v anglickém jazyce
Compositional alteration of polyimide under high fluence implantation by Co+ and Fe+ ions.
Popis výsledku anglicky
Polyimide(PI) foils were implanted with 40 keV Fe+ and Co+ ions to the fluences of 2.5 x 10(16)-1.25 x 10(17) cm(-2) at the ion current densities of 4, 8 and 12 muA cm(-2). Surface morphology and compositional alteration of the implanted polymer have been studied using atomic force microscopy, transmission electron microscopy, Rutherford backscattering and X-ray photoelectron spectroscopy. Carbonisation of the surface layer, followed by oxygen and nitrogen depletion is observed. These processes reach the saturation level at the applied high fluences. A further increase of ion fluence and density of ion current does not change the composition; only an increase in the metal concentration is observed. It is shown that metal ion implantation to high fluence at high ion current density can be effectively employed to form metal/polymer nanocomposites with required parameters.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BG - Jaderná, atomová a molekulová fyzika, urychlovače
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA102%2F01%2F1324" target="_blank" >GA102/01/1324: Dielektrické a elektrické vlastnosti polymerních kompozitů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2003
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Surface Science
ISSN
0039-6028
e-ISSN
—
Svazek periodika
532
Číslo periodika v rámci svazku
N/A
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
6
Strana od-do
1034-1039
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—