SANS investigations of pore anisotropy in superplastically deformed

Popis výsledku v původním jazyce

Superplastically deformed samples of 3 mol% yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) and 3Y-TZP with 20wt% of Al2O3 were studied by SANS with the aim to compare cavitation behaviours under different deformation conditions. Though the average size of cavities formed during deformation is so large that they can be measured only by high-resolution SANS techniques, conventional SANS method permitted us to measure their specific surface and aspect ratio quite effectively. Analysis of the 2-dimentional SANS data clearly showed two qualitatively different cavitation regimes corresponding to the low stress (low strain-rate and high temperature) and high stress conditions, respectively. In the latter case, a new type of flat pores transversalto the tension axis was observed, in addition to the usually present slightly prolate cavities.

Název v anglickém jazyce

SANS investigations of pore anisotropy in superplastically deformed

Popis výsledku anglicky

Superplastically deformed samples of 3 mol% yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) and 3Y-TZP with 20wt% of Al2O3 were studied by SANS with the aim to compare cavitation behaviours under different deformation conditions. Though the average size of cavities formed during deformation is so large that they can be measured only by high-resolution SANS techniques, conventional SANS method permitted us to measure their specific surface and aspect ratio quite effectively. Analysis of the 2-dimentional SANS data clearly showed two qualitatively different cavitation regimes corresponding to the low stress (low strain-rate and high temperature) and high stress conditions, respectively. In the latter case, a new type of flat pores transversalto the tension axis was observed, in addition to the usually present slightly prolate cavities.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica

ISSN

0921-4526

e-ISSN

—

Svazek periodika

350

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

2

Strana od-do

"e1019"-"e1020"

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—