Název v původním jazyce

Small-angle neutron scattering investigation of gamma ' precipitate morphology evolution in creep-exposed single-crystal Ni-base superalloy CMSX-4

Popis výsledku v původním jazyce

In order to assess the material degradation of exposed gas turbine high temperature components, the creep degraded CMSX-4 single-crystal nickel-base superalloy with two axial orientations [001] and [111] was investigated. Constant load creep tests were conducted in the stress/temperature ranges of 250-780 MPa/750-950 degrees C resulting in rupture time variation from 50 to 4000 h. A combination of scanning electron microscopy and a non-destructive small-angle neutron scattering method (SANS) was used toinvestigate the directional coarsening (rafting) of the gamma' precipitates in relation to the stress and temperature applied as well as to the initial crystallographic orientation of the specimens. The SANS results are discussed in terms of the correlation with the raft development, the axial orientation of specimen, the creep parameters and the mechanical properties.

Název v anglickém jazyce

Small-angle neutron scattering investigation of gamma ' precipitate morphology evolution in creep-exposed single-crystal Ni-base superalloy CMSX-4

Popis výsledku anglicky

In order to assess the material degradation of exposed gas turbine high temperature components, the creep degraded CMSX-4 single-crystal nickel-base superalloy with two axial orientations [001] and [111] was investigated. Constant load creep tests were conducted in the stress/temperature ranges of 250-780 MPa/750-950 degrees C resulting in rupture time variation from 50 to 4000 h. A combination of scanning electron microscopy and a non-destructive small-angle neutron scattering method (SANS) was used toinvestigate the directional coarsening (rafting) of the gamma' precipitates in relation to the stress and temperature applied as well as to the initial crystallographic orientation of the specimens. The SANS results are discussed in terms of the correlation with the raft development, the axial orientation of specimen, the creep parameters and the mechanical properties.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BG - Jaderná, atomová a molekulová fyzika, urychlovače

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Physics-Condensed Matter

ISSN

0953-8984

e-ISSN

—

Svazek periodika

20

Číslo periodika v rámci svazku

10

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

000254101000062

EID výsledku v databázi Scopus

—