SANS Investigation of Y ' Precipitate Morphology Evolution in Creep Exposed Single Crystal Ni base Superalloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F10%3A00347276" target="_blank" >RIV/61389005:_____/10:00347276 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

SANS Investigation of Y ' Precipitate Morphology Evolution in Creep Exposed Single Crystal Ni base Superalloy

Popis výsledku v původním jazyce

The creep degraded nickel base single crystal superalloy CMSX-4 of two axial orientations [001] and [111] was investigated with aim to assess the structure degradation. Constant load creep tests were conducted in the stress/temperature ranges of 250-780MPa/750 - 50 degrees C resulting in rupture time variation from 50 to 4000 hours. A combination of scanning electron microscopy (SEM) and non-destructive small-angle neutron scattering method (SANS) was used to. investigate the directional coarsening (rafting) of the gamma prime (gamma') precipitates in relation to the stress and temperature applied as well as to the initial crystallographic orientation of the specimens. The SANS results are discussed in terms of the correlation with the raft development, the axial orientation of specimen, the creep parameters and the mechanical properties.

Název v anglickém jazyce

SANS Investigation of Y ' Precipitate Morphology Evolution in Creep Exposed Single Crystal Ni base Superalloy

Popis výsledku anglicky

The creep degraded nickel base single crystal superalloy CMSX-4 of two axial orientations [001] and [111] was investigated with aim to assess the structure degradation. Constant load creep tests were conducted in the stress/temperature ranges of 250-780MPa/750 - 50 degrees C resulting in rupture time variation from 50 to 4000 hours. A combination of scanning electron microscopy (SEM) and non-destructive small-angle neutron scattering method (SANS) was used to. investigate the directional coarsening (rafting) of the gamma prime (gamma') precipitates in relation to the stress and temperature applied as well as to the initial crystallographic orientation of the specimens. The SANS results are discussed in terms of the correlation with the raft development, the axial orientation of specimen, the creep parameters and the mechanical properties.

Druh

D - Stať ve sborníku

CEP obor

BG - Jaderná, atomová a molekulová fyzika, urychlovače

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ADVANCED MATERIALS FORUM V, PT 1 AND 2

ISBN

—

ISSN

0255-5476

e-ISSN

—

Počet stran výsledku

12

Strana od-do

—

Název nakladatele

TRANS TECH PUBLICATIONS LTD, LAUBLSRUTISTR 24

Místo vydání

CH-8717 STAFA-ZURICH

Místo konání akce

Lisbon

Datum konání akce

5. 4. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000280763200221