In situ observation of morphological changes of gamma ' precipitates in a pre-deformed single-crystal Ni-base superalloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F11%3A00367053" target="_blank" >RIV/61389005:_____/11:00367053 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1107/S0021889811028147" target="_blank" >http://dx.doi.org/10.1107/S0021889811028147</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1107/S0021889811028147" target="_blank" >10.1107/S0021889811028147</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
In situ observation of morphological changes of gamma ' precipitates in a pre-deformed single-crystal Ni-base superalloy
Popis výsledku v původním jazyce
Exposure of a superalloy to an external load results in anisotropic coarsening of the gamma' precipitates, so-called rafting. It was reported in the past that gamma' rafting can also occur as a result of purely thermal treatment, without the simultaneouspresence of an external load, if the specimen has been pre-deformed at relatively low temperature. The evolution of gamma' morphology in pre-deformed specimens of SCA425 Ni-base superalloy was examined in the present study. Unlike in the previous experiments, the compressive stress was used for pre-straining. In situ small-angle neutron scattering (SANS) was employed, which enabled the determination of the morphology directly at high temperature.
Název v anglickém jazyce
In situ observation of morphological changes of gamma ' precipitates in a pre-deformed single-crystal Ni-base superalloy
Popis výsledku anglicky
Exposure of a superalloy to an external load results in anisotropic coarsening of the gamma' precipitates, so-called rafting. It was reported in the past that gamma' rafting can also occur as a result of purely thermal treatment, without the simultaneouspresence of an external load, if the specimen has been pre-deformed at relatively low temperature. The evolution of gamma' morphology in pre-deformed specimens of SCA425 Ni-base superalloy was examined in the present study. Unlike in the previous experiments, the compressive stress was used for pre-straining. In situ small-angle neutron scattering (SANS) was employed, which enabled the determination of the morphology directly at high temperature.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP204%2F11%2F1453" target="_blank" >GAP204/11/1453: Analýza složek cyklického napětí moderních vysokoteplotně odolných konstrukčních materiálů</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Applied Crystallography
ISSN
0021-8898
e-ISSN
—
Svazek periodika
44
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
10
Strana od-do
935-944
Kód UT WoS článku
000295097800006
EID výsledku v databázi Scopus
—