Structure of injection-molded beta-polypropylene and research perspectives of its degradability.

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F03%3A55033276" target="_blank" >RIV/61389013:_____/03:55033276 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Structure of injection-molded beta-polypropylene and research perspectives of its degradability.
Popis výsledku v původním jazyce
Isotactic polypropylene was modified by a specific beta-nucleator and specimens for structure characterization were prepared by injection molding. Distinctly higher beta-phase content was found in the skin layer as compared to the specimen core. Morphology profiles revealed a thinning of the skin with increasing mold temperature. The degree of surface damage caused by photo-oxidative degradation strongly depended on the morphology.
Název v anglickém jazyce
Structure of injection-molded beta-polypropylene and research perspectives of its degradability.
Popis výsledku anglicky
Isotactic polypropylene was modified by a specific beta-nucleator and specimens for structure characterization were prepared by injection molding. Distinctly higher beta-phase content was found in the skin layer as compared to the specimen core. Morphology profiles revealed a thinning of the skin with increasing mold temperature. The degree of surface damage caused by photo-oxidative degradation strongly depended on the morphology.

Projekt
<a href="/cs/project/GA106%2F02%2F1249" target="_blank" >GA106/02/1249: Mikromechanismy porušování semikrystalických polymerů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2003
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)