Degradabilita vstřikovaného beta-polypropylénu ve vztahu k jeho struktuře
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F04%3A63502347" target="_blank" >RIV/70883521:28110/04:63502347 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Degradability of Injection-Molded Beta-Polypropylenes in Relation to Their Structure
Popis výsledku v původním jazyce
Morphology and structure of injection-molded beta-specimens before and after UV aging were rigorously studied by wide-angle X-ray scattering and light microscopy. It was found that the surface cracks on specimens form circular arcs radiating from the injection gate. This effect was explained as a result of chemi-crystallization, which led to crystallinity increase and consequent surface shrinkage. Furthermore, influence of solidification temperature (that means the mold temperature) on character of mentioned cracks was obvious. Finally, infrared microscopy revealed that degradation profile of beta-iPP injection-molded specimens depended on a morphology character resulting from various solidification temperatures.
Název v anglickém jazyce
Degradability of Injection-Molded Beta-Polypropylenes in Relation to Their Structure
Popis výsledku anglicky
Morphology and structure of injection-molded beta-specimens before and after UV aging were rigorously studied by wide-angle X-ray scattering and light microscopy. It was found that the surface cracks on specimens form circular arcs radiating from the injection gate. This effect was explained as a result of chemi-crystallization, which led to crystallinity increase and consequent surface shrinkage. Furthermore, influence of solidification temperature (that means the mold temperature) on character of mentioned cracks was obvious. Finally, infrared microscopy revealed that degradation profile of beta-iPP injection-molded specimens depended on a morphology character resulting from various solidification temperatures.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GP106%2F03%2FP144" target="_blank" >GP106/03/P144: Optimalizace technologických podmínek procesu tokově indukované krystalizace ve vztahu ke struktuře a vlastnostem výrobků</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
8th International Research/Expert Conferece
ISBN
9958-617-21-8
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
239-242
Název nakladatele
Faculty of Mechanical Engineering
Místo vydání
Zenica
Místo konání akce
Neum
Datum konání akce
15. 9. 2004
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—