Fibre-matrix interface development during high temperature exposition of long fibre reinforced SiOC matrix
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F14%3A00434889" target="_blank" >RIV/61389013:_____/14:00434889 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/14:00434889 RIV/67985891:_____/14:00434889
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.401" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.401</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.401" target="_blank" >10.4028/www.scientific.net/KEM.592-593.401</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fibre-matrix interface development during high temperature exposition of long fibre reinforced SiOC matrix
Popis výsledku v původním jazyce
The fracture behaviour of long fibre reinforced composites is predetermined mainly by properties of fibre-matrix interface. The matrix prepared by pyrolysis of polysiloxane resin possesses ability to resist high temperatures without significant damage under oxidising atmosphere. The application is therefore limited by fibres and possible changes in the fibre matrix interface. The study of development of interface during high temperature exposition is the main aim of this contribution. Application of various techniques as FIB, GIS, TEM, XRD allowed to monitor microstructural changes in the interface of selected places without additional damage caused by preparation. Additionally, it was possible to obtain information about damage, the crack formation, caused by the heat treatment from the fracture mechanics point of view.
Název v anglickém jazyce
Fibre-matrix interface development during high temperature exposition of long fibre reinforced SiOC matrix
Popis výsledku anglicky
The fracture behaviour of long fibre reinforced composites is predetermined mainly by properties of fibre-matrix interface. The matrix prepared by pyrolysis of polysiloxane resin possesses ability to resist high temperatures without significant damage under oxidising atmosphere. The application is therefore limited by fibres and possible changes in the fibre matrix interface. The study of development of interface during high temperature exposition is the main aim of this contribution. Application of various techniques as FIB, GIS, TEM, XRD allowed to monitor microstructural changes in the interface of selected places without additional damage caused by preparation. Additionally, it was possible to obtain information about damage, the crack formation, caused by the heat treatment from the fracture mechanics point of view.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Materials Structure and Micromechanics of Fracture VII
ISBN
978-3-03785-934-6
ISSN
1013-9826
e-ISSN
—
Počet stran výsledku
4
Strana od-do
401-404
Název nakladatele
Trans Tech Publications
Místo vydání
Zurich
Místo konání akce
Brno
Datum konání akce
1. 7. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000336694400088