Si-O-C ceramic foams derived from polymethylphenylsiloxane precursor with starch as foaming agent

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F15%3A00448254" target="_blank" >RIV/61389013:_____/15:00448254 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/15:00448254 RIV/67985891:_____/15:00448254

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2015.04.032" target="_blank" >http://dx.doi.org/10.1016/j.jeurceramsoc.2015.04.032</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2015.04.032" target="_blank" >10.1016/j.jeurceramsoc.2015.04.032</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Si-O-C ceramic foams derived from polymethylphenylsiloxane precursor with starch as foaming agent

Popis výsledku v původním jazyce

Si-O-C ("black glass") ceramic foam was prepared by the foaming of a preceramic polymer, polymethylphenylsiloxane resin, and by its subsequent pyrolysis conducted up to 1000 degrees C. Prior to foaming, corn starch was blended with the diluted resin, inorder to achieve uniform and small-sized pores. The foaming of the polymer blend was carried out simultaneously with its crosslinldng: escaping water vapour (forming from starch) served as the blowing agent. The apparent foam density can be controlled byadjusting the foaming temperature or by varying the amount of added starch. Both ways were used to prepare foam samples with porosity in the range of 70-90%. The porosity-dependent compressive strength of these foams was found to be in the range of 1-16MPa. (C) 2015 Elsevier Ltd. All rights reserved.

Název v anglickém jazyce

Si-O-C ceramic foams derived from polymethylphenylsiloxane precursor with starch as foaming agent

Popis výsledku anglicky

Si-O-C ("black glass") ceramic foam was prepared by the foaming of a preceramic polymer, polymethylphenylsiloxane resin, and by its subsequent pyrolysis conducted up to 1000 degrees C. Prior to foaming, corn starch was blended with the diluted resin, inorder to achieve uniform and small-sized pores. The foaming of the polymer blend was carried out simultaneously with its crosslinldng: escaping water vapour (forming from starch) served as the blowing agent. The apparent foam density can be controlled byadjusting the foaming temperature or by varying the amount of added starch. Both ways were used to prepare foam samples with porosity in the range of 70-90%. The porosity-dependent compressive strength of these foams was found to be in the range of 1-16MPa. (C) 2015 Elsevier Ltd. All rights reserved.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F12%2F2445" target="_blank" >GAP107/12/2445: SiOC keramická pěna z pyrolyzovaného polymerního prekurzoru jako jádro tepelně odolných sendvičových struktur</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

35

Číslo periodika v rámci svazku

13

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

3427-3436

Kód UT WoS článku

000359029300008

EID výsledku v databázi Scopus

2-s2.0-84937523126