Zlepšení mechanických vlastností plazmových nástřiků oxidů hlinitého a zirkoničitého dosažené pomocí dodatečného ovlivnění laserem

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F05%3A00025702" target="_blank" >RIV/61389021:_____/05:00025702 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Improvement of mechanical properties of Alumina and Zirconia plasma sprayed coatings induced by laser after-treatment

Popis výsledku v původním jazyce

Alumina and stabilized Zirconia were plasma sprayed in air using the water-stabilized plasma torch. In the case of Alumina two different stand-off distances were applied at spraying. Nd-YAG laser was then used for additional treatment of plasma sprayed coatings. The laser was maintained in a quasi-continual regime and defocused from the surface to increase the treated coating's area. Energy density was varied together with the laser scanning velocity to ensure variance in thermal history of the treatedsurfaces. Microhardness, surface roughness and slurry abrasion resistance (SAR) were measured before and after the laser treatment. Results vary in dependence on the laser treatment's parameters. When the treatment results in substantial changes of the structure (up to a complete re-melting of the surface), enhancement of all measured properties was proven.

Název v anglickém jazyce

Improvement of mechanical properties of Alumina and Zirconia plasma sprayed coatings induced by laser after-treatment

Popis výsledku anglicky

Alumina and stabilized Zirconia were plasma sprayed in air using the water-stabilized plasma torch. In the case of Alumina two different stand-off distances were applied at spraying. Nd-YAG laser was then used for additional treatment of plasma sprayed coatings. The laser was maintained in a quasi-continual regime and defocused from the surface to increase the treated coating's area. Energy density was varied together with the laser scanning velocity to ensure variance in thermal history of the treatedsurfaces. Microhardness, surface roughness and slurry abrasion resistance (SAR) were measured before and after the laser treatment. Results vary in dependence on the laser treatment's parameters. When the treatment results in substantial changes of the structure (up to a complete re-melting of the surface), enhancement of all measured properties was proven.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/KSK1010104" target="_blank" >KSK1010104: Fyzika kondenzovaných systémů a materiálový výzkum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of International Thermal Spray Conference 2005

ISBN

3-87155-793-5

ISSN

—

e-ISSN

—

Počet stran výsledku

12

Strana od-do

1033-1038

Název nakladatele

DVS-Verlag, Dusseldorf

Místo vydání

Dusseldorf

Místo konání akce

Basilej

Datum konání akce

2. 5. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—