Zlepšení mechanických vlastností plazmových nástřiků oxidu hlinitého a oxidu zirkoničitého dosažené následným přetavením pomocí laseru

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F07%3A00097067" target="_blank" >RIV/61389021:_____/07:00097067 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

IMPROVEMENT OF MECHANICAL PROPERTIES OF ALUMINA AND ZIRCONIA PLASMA SPRAYED COATINGS INDUCED BY LASER POST-TREATMENT

Popis výsledku v původním jazyce

Alumina and stabilized zirconia were plasma sprayed in air using a water-stabilized plasma torch. Nd-YAG laser was then used for additional treatment of the plasma sprayed coatings. The laser was maintained in a quasi-continual regime and defocused fromthe surface to increase the treated area. Energy density was varied together with the laser scanning velocity to ensure variance in thermal history of the treated surfaces. Microhardness, surface roughness and slurry abrasion resistance (SAR) were measured before and after the laser treatment. Results vary in dependence on the laser treatment parameters. When the laser treatment resulted in substantial changes of the structure (up to a complete re-melting of the surface), enhancement of all measured properties was proven. It is demonstrated that the change of the mechanical properties can be correlated with the optical properties of the coating materials at the laser wavelength.

Název v anglickém jazyce

IMPROVEMENT OF MECHANICAL PROPERTIES OF ALUMINA AND ZIRCONIA PLASMA SPRAYED COATINGS INDUCED BY LASER POST-TREATMENT

Popis výsledku anglicky

Alumina and stabilized zirconia were plasma sprayed in air using a water-stabilized plasma torch. Nd-YAG laser was then used for additional treatment of the plasma sprayed coatings. The laser was maintained in a quasi-continual regime and defocused fromthe surface to increase the treated area. Energy density was varied together with the laser scanning velocity to ensure variance in thermal history of the treated surfaces. Microhardness, surface roughness and slurry abrasion resistance (SAR) were measured before and after the laser treatment. Results vary in dependence on the laser treatment parameters. When the laser treatment resulted in substantial changes of the structure (up to a complete re-melting of the surface), enhancement of all measured properties was proven. It is demonstrated that the change of the mechanical properties can be correlated with the optical properties of the coating materials at the laser wavelength.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/1QS200430560" target="_blank" >1QS200430560: Progresivní žárové nástřiky odolné proti otěru</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics - Silikáty

ISSN

0862-5468

e-ISSN

—

Svazek periodika

51

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

9

Strana od-do

181-189

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—