Bulk nanocrystalline ceramic material prepared by plasma spraying

Popis výsledku v původním jazyce

Ceramic material based on alumina-zirconia mixture have been successfully plasma sprayed by water stabilized plasma torch (WSP(R)). The material is composed of three main compounds Al2O3, ZrO2, and SiO2 where the ratio of Al2O3 ? ZrO2 compounds is closeto the ratio in their respective eutectic alloy. The material is a refractory and exhibits very high hardness, abrasion resistance, and chemical resistance. Cast tiles of the original material were ground and sieved to obtain the right powder cut size for plasma spraying by WSP(R). Both thick coatings and free standing parts with very low open porosity were easily achieved by WSP(R). The feedstock powder is mostly crystalline whereas the as?sprayed material is mostly amorphous with some unmelted crystalline particles present. Electron microscopy and X-ray diffraction were employed to determine microstructure, crystallinity, and phase content of the bulk samples as well as individual splats.

Název v anglickém jazyce

Bulk nanocrystalline ceramic material prepared by plasma spraying

Popis výsledku anglicky

Ceramic material based on alumina-zirconia mixture have been successfully plasma sprayed by water stabilized plasma torch (WSP(R)). The material is composed of three main compounds Al2O3, ZrO2, and SiO2 where the ratio of Al2O3 ? ZrO2 compounds is closeto the ratio in their respective eutectic alloy. The material is a refractory and exhibits very high hardness, abrasion resistance, and chemical resistance. Cast tiles of the original material were ground and sieved to obtain the right powder cut size for plasma spraying by WSP(R). Both thick coatings and free standing parts with very low open porosity were easily achieved by WSP(R). The feedstock powder is mostly crystalline whereas the as?sprayed material is mostly amorphous with some unmelted crystalline particles present. Electron microscopy and X-ray diffraction were employed to determine microstructure, crystallinity, and phase content of the bulk samples as well as individual splats.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F04%2FP012" target="_blank" >GP106/04/P012: Vývoj keramických nástřiků během jejich vytváření pomocí plazmového stříkání</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANO ?05 International Conference Proceedings

ISBN

80-214-3085-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

201-206

Název nakladatele

—

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

8. 11. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—