Název v původním jazyce

BULK NANOCRYSTALLINE ALUMINA-ZIRCONIA MATERIALS

Popis výsledku v původním jazyce

An alternative method to produce bulk nanocrystalline materials is to produce amorphous material by rapid solidification and then by controlled crystallization introduce nanocrystalline structure. One technique capable of achieving rapid solidification in materials is plasma spraying. Feedstock material for plasma spraying was composed of about 15 wt.% of SiO2 in addition to the near eutectic ratio of Al2O3 and ZrO2 compounds. Amorphous coatings and free standing parts from this material prepared by water stabilized plasma torch (WSP) exhibit very low porosity and high hardness. When heat treated, the as-sprayed material crystallizes just above 950?C with an associated volume shrinkage of 1.8%. The volume shrinkage does not cause material breakup. Short heat treatment of the as-sprayed material produces a very fine nanocomposite structure within each splat. Each splat contains nanocrystallites with average size as small as 13 nm.

Název v anglickém jazyce

BULK NANOCRYSTALLINE ALUMINA-ZIRCONIA MATERIALS

Popis výsledku anglicky

An alternative method to produce bulk nanocrystalline materials is to produce amorphous material by rapid solidification and then by controlled crystallization introduce nanocrystalline structure. One technique capable of achieving rapid solidification in materials is plasma spraying. Feedstock material for plasma spraying was composed of about 15 wt.% of SiO2 in addition to the near eutectic ratio of Al2O3 and ZrO2 compounds. Amorphous coatings and free standing parts from this material prepared by water stabilized plasma torch (WSP) exhibit very low porosity and high hardness. When heat treated, the as-sprayed material crystallizes just above 950?C with an associated volume shrinkage of 1.8%. The volume shrinkage does not cause material breakup. Short heat treatment of the as-sprayed material produces a very fine nanocomposite structure within each splat. Each splat contains nanocrystallites with average size as small as 13 nm.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN300430651" target="_blank" >KAN300430651: Nanokrystalizace plazmových nástřiků na bázi eutektických směsí keramik</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings 8th multinational congress on microscopy

ISBN

978-80-239-9397-4

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

141-142

Název nakladatele

Czechoslovak microscopy society

Místo vydání

České Budějovice

Místo konání akce

Prague

Datum konání akce

17. 6. 2007

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—