Fabrication of Bulk Nanocrystalline Ceramic Materials

Popis výsledku v původním jazyce

An alternative method to produce bulk nanocrystalline materials is to produce amorphous material by rapid solidification followed by controlled solid state crystallization. Four different materials studied in this work are based on near-eutectic mixturesof alumina, zirconia, and silica. Powder feedstock materials have been plasma sprayed using a water stabilized plasma torch (WSP) and subsequently heat-treated to prepare materials with nanocrystallites of 12 nm diameter on average. The as-sprayed materials have very low porosity and are mostly amorphous. The as-sprayed amorphous materials crystallize at temperatures around 950 ?C. The resulting structure is best described as nanocomposite with the very small crystallites embedded in an amorphous matrix. The role of silica on phase composition, microstructure, and mechanical properties of the as-sprayed and annealed materials is discussed. The as-sprayed amorphous materials exhibit high hardness and high abrasion resistance.

Název v anglickém jazyce

Fabrication of Bulk Nanocrystalline Ceramic Materials

Popis výsledku anglicky

An alternative method to produce bulk nanocrystalline materials is to produce amorphous material by rapid solidification followed by controlled solid state crystallization. Four different materials studied in this work are based on near-eutectic mixturesof alumina, zirconia, and silica. Powder feedstock materials have been plasma sprayed using a water stabilized plasma torch (WSP) and subsequently heat-treated to prepare materials with nanocrystallites of 12 nm diameter on average. The as-sprayed materials have very low porosity and are mostly amorphous. The as-sprayed amorphous materials crystallize at temperatures around 950 ?C. The resulting structure is best described as nanocomposite with the very small crystallites embedded in an amorphous matrix. The role of silica on phase composition, microstructure, and mechanical properties of the as-sprayed and annealed materials is discussed. The as-sprayed amorphous materials exhibit high hardness and high abrasion resistance.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN300430651" target="_blank" >KAN300430651: Nanokrystalizace plazmových nástřiků na bázi eutektických směsí keramik</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Thermal Spray Technology

ISSN

1059-9630

e-ISSN

—

Svazek periodika

17

Číslo periodika v rámci svazku

5-6

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

000261411700041

EID výsledku v databázi Scopus

—