Preparation of tungsten filters and membranes
Popis výsledku v původním jazyce
Tungsten filters and membranes were prepared by three different techniques and their mechanical properties and filtering ability were compared. The preparation consisted of sintering spherical tungsten powders of narrow size classes by common metal filter production technologies. The spherical tungsten powders were prepared by a simple technology. Tungsten powder of a narrow size distribution was injected in a plasma jet generated by a water stabilized plasma torch WSP?, based on the Gerdien arc principle, operating under 160 kW. Prior to sintering, the powders were compacted into cylindrical plates under 100 MPa pressure with a temporary binder ? 6 wt% AC 112 acrylate suspension. First set was prepared by hot isostatic sintering in ASEA HIP D 320 apparatus at 1750°C temperature and in an argone protective atmosphere. Second set was prepared by the gravity sintering technique at the same temperature. Third set was prepared by high pressure compacting in a BELT type apparatus.
Název v anglickém jazyce
Preparation of tungsten filters and membranes
Popis výsledku anglicky
Tungsten filters and membranes were prepared by three different techniques and their mechanical properties and filtering ability were compared. The preparation consisted of sintering spherical tungsten powders of narrow size classes by common metal filter production technologies. The spherical tungsten powders were prepared by a simple technology. Tungsten powder of a narrow size distribution was injected in a plasma jet generated by a water stabilized plasma torch WSP?, based on the Gerdien arc principle, operating under 160 kW. Prior to sintering, the powders were compacted into cylindrical plates under 100 MPa pressure with a temporary binder ? 6 wt% AC 112 acrylate suspension. First set was prepared by hot isostatic sintering in ASEA HIP D 320 apparatus at 1750°C temperature and in an argone protective atmosphere. Second set was prepared by the gravity sintering technique at the same temperature. Third set was prepared by high pressure compacting in a BELT type apparatus.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings 9th International Conference on Inorganic Membranes 9ICIM
ISBN
9788214040265
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
637-640
Název nakladatele
Ed.Bredesen & Raeder, SINTEF, Norway
Místo vydání
Lillehammer - Norway
Místo konání akce
Lillehammer, Norway
Datum konání akce
25. 6. 2006
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—