Crystallization kinetics of amorphous alumina?zirconia?silica ceramics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F09%3A00329728" target="_blank" >RIV/61389021:_____/09:00329728 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388980:_____/09:00329728

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crystallization kinetics of amorphous alumina?zirconia?silica ceramics

Popis výsledku v původním jazyce

Crystallization kinetics of amorphous alumina?zirconia?silica ceramics was studied by nonisothermal differential scanning calorimetry (DSC). Different amorphous materials were produced by plasma spraying of near-eutectic Al2O3?ZrO2?SiO2 mixtures. Phase composition and microstructure of the amorphous materials and nanocrystalline products were analyzed. All of the investigated materials show an exothermic peak between 940 and 990 C in the DSC experiments. The activation energies calculated from DSC traces decrease with increasing SiO2 concentration. Values of the Avrami coefficients together with results of the microstructural observations indicate that tetragonal zirconia crystallization from materials containing more than 10 wt.% SiO2 proceeds by a diffusion-controlled mechanism with nucleation occurring predominantly at the beginning of the process.

Název v anglickém jazyce

Crystallization kinetics of amorphous alumina?zirconia?silica ceramics

Popis výsledku anglicky

Crystallization kinetics of amorphous alumina?zirconia?silica ceramics was studied by nonisothermal differential scanning calorimetry (DSC). Different amorphous materials were produced by plasma spraying of near-eutectic Al2O3?ZrO2?SiO2 mixtures. Phase composition and microstructure of the amorphous materials and nanocrystalline products were analyzed. All of the investigated materials show an exothermic peak between 940 and 990 C in the DSC experiments. The activation energies calculated from DSC traces decrease with increasing SiO2 concentration. Values of the Avrami coefficients together with results of the microstructural observations indicate that tetragonal zirconia crystallization from materials containing more than 10 wt.% SiO2 proceeds by a diffusion-controlled mechanism with nucleation occurring predominantly at the beginning of the process.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN300430651" target="_blank" >KAN300430651: Nanokrystalizace plazmových nástřiků na bázi eutektických směsí keramik</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

29

Číslo periodika v rámci svazku

15

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000270162100007

EID výsledku v databázi Scopus

—