Crystallization kinetics of amorphous alumina zirconia silica ceramics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F09%3A00336711" target="_blank" >RIV/61389021:_____/09:00336711 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388980:_____/09:00336711

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crystallization kinetics of amorphous alumina zirconia silica ceramics

Popis výsledku v původním jazyce

Crystallization of amorphous alumina?zirconia?silica ceramics was studied for seven different amorphous materials produced by plasma spraying. The activation energies calculated from DSC traces decrease with increasing SiO2 concentration from 1500 to 900kJ/mol. Values of the Avrami coefficients together with results of the microstructural observations indicate that tetragonal zirconia crystallization from materials containing more than 10 wt.% SiO2 proceeds by a diffusion-controlled mechanism with nucleation occurring predominantly at the beginning of the process. Material with almost no SiO2 exhibited a value of the Avrami exponent consistent with the crystal growth governed by processes at the phase boundary.

Název v anglickém jazyce

Crystallization kinetics of amorphous alumina zirconia silica ceramics

Popis výsledku anglicky

Crystallization of amorphous alumina?zirconia?silica ceramics was studied for seven different amorphous materials produced by plasma spraying. The activation energies calculated from DSC traces decrease with increasing SiO2 concentration from 1500 to 900kJ/mol. Values of the Avrami coefficients together with results of the microstructural observations indicate that tetragonal zirconia crystallization from materials containing more than 10 wt.% SiO2 proceeds by a diffusion-controlled mechanism with nucleation occurring predominantly at the beginning of the process. Material with almost no SiO2 exhibited a value of the Avrami exponent consistent with the crystal growth governed by processes at the phase boundary.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN300430651" target="_blank" >KAN300430651: Nanokrystalizace plazmových nástřiků na bázi eutektických směsí keramik</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Microscopy and Microanalysis

ISSN

1431-9276

e-ISSN

—

Svazek periodika

15

Číslo periodika v rámci svazku

S2

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

2

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—