Analysis of powder particles of high carbon cast iron after air plasma spraying

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F09%3A00341008" target="_blank" >RIV/61389021:_____/09:00341008 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/09:00341008

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of powder particles of high carbon cast iron after air plasma spraying

Popis výsledku v původním jazyce

Structure and phase analysis of high carbon cast iron prepared by plasma spraying was performed using X-ray diffraction and Mössbauer spectroscopy. The sprayed powder particles were trapped in liquid nitrogen to fix their composition during the flight from the plasma torch. The results show decarburization and oxidation of the powder. The carbon content decrease is more pronounced on surfaces of the particles. The fresh powder exhibits an anomalous magnetic transition from ferromagnetic to paramagneticstate during the sample cooling from room temperature down to 28 K. This effect was explained as result of high concentration of defects and strains. The long time ageing at room temperature caused transition to more stable phase composition and diminishing of the anomalous magnetic transition.

Název v anglickém jazyce

Analysis of powder particles of high carbon cast iron after air plasma spraying

Popis výsledku anglicky

Structure and phase analysis of high carbon cast iron prepared by plasma spraying was performed using X-ray diffraction and Mössbauer spectroscopy. The sprayed powder particles were trapped in liquid nitrogen to fix their composition during the flight from the plasma torch. The results show decarburization and oxidation of the powder. The carbon content decrease is more pronounced on surfaces of the particles. The fresh powder exhibits an anomalous magnetic transition from ferromagnetic to paramagneticstate during the sample cooling from room temperature down to 28 K. This effect was explained as result of high concentration of defects and strains. The long time ageing at room temperature caused transition to more stable phase composition and diminishing of the anomalous magnetic transition.

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA1041404" target="_blank" >IAA1041404: Atomové uspořádání u povrchů a rozhraní slitin 3d kovů.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ISIAME 2008

ISBN

978-3-642-01369-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Springer

Místo vydání

New York

Místo konání akce

Budapest

Datum konání akce

17. 8. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000273775100004