Fatigue Performance of TBCs on Hastelloy X Substrate during Cyclic Bending

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F15%3A00454450" target="_blank" >RIV/61389021:_____/15:00454450 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue Performance of TBCs on Hastelloy X Substrate during Cyclic Bending

Popis výsledku v původním jazyce

Our previous experiments with low-cost steel substrates confirmed that individual steps of conventional thermal barrier coating (TBC) deposition may influence fatigue properties of the coated samples differently. In this study, testing was carried out for TBC samples deposited on industrially more relevant Hastelloy X substrates. Samples were tested after each step of TBC deposition process: as-received (noncoated), grit-blasted, bond-coated (NiCoCrAlY) and bondcoated + top-coated (yttria-stabilized zirconia - YSZ). Conventional atmospheric plasma spraying (APS) with gas stabilized plasma torch was used for deposition of both bond coat and top coat. In addition, for one half of the samples, bond coat was prepared by consecutive combination of HVAF (High Velocity Air Fuel) and APS processes...

Název v anglickém jazyce

Fatigue Performance of TBCs on Hastelloy X Substrate during Cyclic Bending

Popis výsledku anglicky

Our previous experiments with low-cost steel substrates confirmed that individual steps of conventional thermal barrier coating (TBC) deposition may influence fatigue properties of the coated samples differently. In this study, testing was carried out for TBC samples deposited on industrially more relevant Hastelloy X substrates. Samples were tested after each step of TBC deposition process: as-received (noncoated), grit-blasted, bond-coated (NiCoCrAlY) and bondcoated + top-coated (yttria-stabilized zirconia - YSZ). Conventional atmospheric plasma spraying (APS) with gas stabilized plasma torch was used for deposition of both bond coat and top coat. In addition, for one half of the samples, bond coat was prepared by consecutive combination of HVAF (High Velocity Air Fuel) and APS processes...

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Thermal Spray 2015: Proceedings from the International Thermal Spray Conference

ISBN

978-1-62708-093-4

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

406-412

Název nakladatele

ASM International

Místo vydání

Materials Park, OH

Místo konání akce

Long Beach, California

Datum konání akce

11. 5. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—