Failure analysis of thermally cycled columnar thermal barrier coatings produced by high-velocity-air fuel and axial-suspension-plasma spraying: A design perspective

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F18%3A00489520" target="_blank" >RIV/61389021:_____/18:00489520 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.ceramint.2017.11.084" target="_blank" >http://dx.doi.org/10.1016/j.ceramint.2017.11.084</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ceramint.2017.11.084" target="_blank" >10.1016/j.ceramint.2017.11.084</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Failure analysis of thermally cycled columnar thermal barrier coatings produced by high-velocity-air fuel and axial-suspension-plasma spraying: A design perspective

Popis výsledku v původním jazyce

Axial-suspension-plasma spraying (ASPS) is a fairly recent thermal spray technology which enables production of ceramic top coats in TBCs, incorporating simultaneously the properties of both the conventional-plasma sprayed (highly insulating porous structures) and electron-beam-physical-vapor-deposited (strain-tolerant columnar structures) top coats. TBCs are required to insulate the hot components in a gas turbine engine against high temperature and harsh operating conditions. Periodic heating and cooling of turbine engines during operation can create severe thermal cyclic fatigue conditions which can degrade the performance of these coatings eventually leading to the failure. An in-depth experimental investigation was performed to understand the failure behavior of columnar TBCs subjected to thermal cyclic fatigue (TCF) test at 1100 degrees C. The study revealed that the TCF performance was influenced to an extent, by the top coat microstructure, but was primarily affected by the severity of thermally grown oxide (TGO) growth at the bond coat-top coat interface. Mixed failure modes comprising crack propagation through the bond coat-TGO interface, through TGO and within the top coat were identified. Based on the analysis of the experimental results and thorough discussion a novel design of microstructure for the high TCF performance columnar TBC is proposed.

Název v anglickém jazyce

Failure analysis of thermally cycled columnar thermal barrier coatings produced by high-velocity-air fuel and axial-suspension-plasma spraying: A design perspective

Popis výsledku anglicky

Axial-suspension-plasma spraying (ASPS) is a fairly recent thermal spray technology which enables production of ceramic top coats in TBCs, incorporating simultaneously the properties of both the conventional-plasma sprayed (highly insulating porous structures) and electron-beam-physical-vapor-deposited (strain-tolerant columnar structures) top coats. TBCs are required to insulate the hot components in a gas turbine engine against high temperature and harsh operating conditions. Periodic heating and cooling of turbine engines during operation can create severe thermal cyclic fatigue conditions which can degrade the performance of these coatings eventually leading to the failure. An in-depth experimental investigation was performed to understand the failure behavior of columnar TBCs subjected to thermal cyclic fatigue (TCF) test at 1100 degrees C. The study revealed that the TCF performance was influenced to an extent, by the top coat microstructure, but was primarily affected by the severity of thermally grown oxide (TGO) growth at the bond coat-top coat interface. Mixed failure modes comprising crack propagation through the bond coat-TGO interface, through TGO and within the top coat were identified. Based on the analysis of the experimental results and thorough discussion a novel design of microstructure for the high TCF performance columnar TBC is proposed.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics International

ISSN

0272-8842

e-ISSN

—

Svazek periodika

44

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

12

Strana od-do

3161-3172

Kód UT WoS článku

000423891900070

EID výsledku v databázi Scopus

2-s2.0-85034822127