The origin and the effect of the fcc phase in sintered HfNbTaTiZr
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F21%3A00538131" target="_blank" >RIV/61389021:_____/21:00538131 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68378271:_____/21:00538131 RIV/00216208:11320/21:10439052
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/abs/pii/S0167577X20319327?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/abs/pii/S0167577X20319327?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matlet.2020.129224" target="_blank" >10.1016/j.matlet.2020.129224</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The origin and the effect of the fcc phase in sintered HfNbTaTiZr
Popis výsledku v původním jazyce
The growing interest in preparing refractory high entropy alloys via powder metallurgy reveals significant sensitivity to impurities, influencing the phase composition and microstructure and, consequently, the mechanical properties. Mechanical alloying of commercial purity powders is a cost-effective way of material preparation leading to a very fine microstructure when spark plasma sintering is used. However, the atmosphere of the milling process plays a significant role. This study shows that the phase composition of the HfNbTaTiZr alloy may be tailored by milling in ambient atmosphere, in argon or in nitrogen. Formation of a new fcc-ZrHfTi phase as a complex nitrogen and oxygen compound was elucidated and its significant hardening effect was shown. Finally, exceptional hardness was achieved by the synergic effect of nano-grained structure and high volume fraction of fcc-ZrHfTi phase.
Název v anglickém jazyce
The origin and the effect of the fcc phase in sintered HfNbTaTiZr
Popis výsledku anglicky
The growing interest in preparing refractory high entropy alloys via powder metallurgy reveals significant sensitivity to impurities, influencing the phase composition and microstructure and, consequently, the mechanical properties. Mechanical alloying of commercial purity powders is a cost-effective way of material preparation leading to a very fine microstructure when spark plasma sintering is used. However, the atmosphere of the milling process plays a significant role. This study shows that the phase composition of the HfNbTaTiZr alloy may be tailored by milling in ambient atmosphere, in argon or in nitrogen. Formation of a new fcc-ZrHfTi phase as a complex nitrogen and oxygen compound was elucidated and its significant hardening effect was shown. Finally, exceptional hardness was achieved by the synergic effect of nano-grained structure and high volume fraction of fcc-ZrHfTi phase.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Letters
ISSN
0167-577X
e-ISSN
—
Svazek periodika
286
Číslo periodika v rámci svazku
March
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
129224
Kód UT WoS článku
000615986100026
EID výsledku v databázi Scopus
2-s2.0-85098124278