Cellulose acetate-based carbon xerogels and cryogels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61988987%3A17310%2F13%3AA14017VP" target="_blank" >RIV/61988987:17310/13:A14017VP - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Cellulose acetate-based carbon xerogels and cryogels

Popis výsledku v původním jazyce

Low density carbonaceous materials based on biosources were prepared from cellulose acetate with a catalyst and a crosslinking agent. Standard preparation of these materials included dissolution, gelation and subsequent drying. In this study, cellulose acetate xerogels or cryogels were prepared, and the influence of the different drying techniques applied was investigated. The internal surface area of cellulose xerogels and cryogels varied from 700 to 850 m2 g-1, the volume of pores was 0.3 ml g-1. Other properties such as thermal decomposition or surface chemistry were gained and both materials were analysed by adsorption experiments of selected heavy metal and organic dye from aqueous phase.

Název v anglickém jazyce

Cellulose acetate-based carbon xerogels and cryogels

Popis výsledku anglicky

Low density carbonaceous materials based on biosources were prepared from cellulose acetate with a catalyst and a crosslinking agent. Standard preparation of these materials included dissolution, gelation and subsequent drying. In this study, cellulose acetate xerogels or cryogels were prepared, and the influence of the different drying techniques applied was investigated. The internal surface area of cellulose xerogels and cryogels varied from 700 to 850 m2 g-1, the volume of pores was 0.3 ml g-1. Other properties such as thermal decomposition or surface chemistry were gained and both materials were analysed by adsorption experiments of selected heavy metal and organic dye from aqueous phase.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CB - Analytická chemie, separace

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Characterisation VI

ISSN

1743-3533

e-ISSN

—

Svazek periodika

77

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

11

Strana od-do

65-75

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—