Reproducibility of preparation of cellulose-based cryogels characterised by TG-MS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61988987%3A17310%2F15%3AA1501CMI" target="_blank" >RIV/61988987:17310/15:A1501CMI - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Reproducibility of preparation of cellulose-based cryogels characterised by TG-MS
Popis výsledku v původním jazyce
Abstract A TG-MS analysis was applied to reveal the reproducibility of preparation of cellulose-based cryogels. The cellulose materials were obtained by dissolution of cellulose in melted Ca(SCN) 2 , followed by gelation and regeneration in an ethanol bath and dried by lyophilisation. The whole preparation process was repeated 14 times. The pyrolysis of the prepared samples was investigated by TG- MS. A number of parameters were determined from the obtained TG, DSC and MS curves and statistically ana- lysed. TG and MS data together with estimated reactions which occurred during sample decomposition enable the calculation of the composition of cryogels and pyrolysed material. An unexpected amount of calcium thiocyanate was found in cellulose cryogels (about 31 %) and after pyrolysis, a high content of calcium oxide (about 58 %) as a product of calcium thiocyanate decomposition was cal- culated for the final material.
Název v anglickém jazyce
Reproducibility of preparation of cellulose-based cryogels characterised by TG-MS
Popis výsledku anglicky
Abstract A TG-MS analysis was applied to reveal the reproducibility of preparation of cellulose-based cryogels. The cellulose materials were obtained by dissolution of cellulose in melted Ca(SCN) 2 , followed by gelation and regeneration in an ethanol bath and dried by lyophilisation. The whole preparation process was repeated 14 times. The pyrolysis of the prepared samples was investigated by TG- MS. A number of parameters were determined from the obtained TG, DSC and MS curves and statistically ana- lysed. TG and MS data together with estimated reactions which occurred during sample decomposition enable the calculation of the composition of cryogels and pyrolysed material. An unexpected amount of calcium thiocyanate was found in cellulose cryogels (about 31 %) and after pyrolysis, a high content of calcium oxide (about 58 %) as a product of calcium thiocyanate decomposition was cal- culated for the final material.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CB - Analytická chemie, separace
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1208" target="_blank" >LO1208: Teoretické aspekty energetického zpracování odpadů a ochrany prostředí před negativními dopady</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Thermal Analysis and Calorimetry
ISSN
1388-6150
e-ISSN
—
Svazek periodika
1
Číslo periodika v rámci svazku
119
Stát vydavatele periodika
HU - Maďarsko
Počet stran výsledku
9
Strana od-do
359-367
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—