Stochastic Estimation of Corrosion Propagation Time for HPC Mixtures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27120%2F12%3A86083401" target="_blank" >RIV/61989100:27120/12:86083401 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Stochastic Estimation of Corrosion Propagation Time for HPC Mixtures

Popis výsledku v původním jazyce

The chloride induced corrosion of steel reinforcement embedded in concrete is a significant issue that threatens the service life of exposed concrete structures. This service life is generally divided into two phases; namely the initiation period and thepropagation period. This paper presents a contribution to determine concrete cover cracking time based on the concept of critical corrosion products, penetration depth and degradation of steel reinforcement. Electrical resistivity values of high-performance concrete (HPC) mixtures with different binary and ternary cementitious combinations were used to compute concrete cover cracking time. The stochastic approach uses?Korozeeneck? software to simulate multiple parameters that govern the corrosion, accounting for uncertainties associated with measured histograms of real data. Results from the probabilistic analysis predicted that the HPC mixtures greatly delayed concrete cover cracking time compared with the control and OPC mixtures and

Název v anglickém jazyce

Stochastic Estimation of Corrosion Propagation Time for HPC Mixtures

Popis výsledku anglicky

The chloride induced corrosion of steel reinforcement embedded in concrete is a significant issue that threatens the service life of exposed concrete structures. This service life is generally divided into two phases; namely the initiation period and thepropagation period. This paper presents a contribution to determine concrete cover cracking time based on the concept of critical corrosion products, penetration depth and degradation of steel reinforcement. Electrical resistivity values of high-performance concrete (HPC) mixtures with different binary and ternary cementitious combinations were used to compute concrete cover cracking time. The stochastic approach uses?Korozeeneck? software to simulate multiple parameters that govern the corrosion, accounting for uncertainties associated with measured histograms of real data. Results from the probabilistic analysis predicted that the HPC mixtures greatly delayed concrete cover cracking time compared with the control and OPC mixtures and

Druh

D - Stať ve sborníku

CEP obor

JM - Inženýrské stavitelství

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.20.0013" target="_blank" >EE2.3.20.0013: Tvorba a internacionalizace špičkových vědeckých týmů a zvyšování jejich excelence na Fakultě stavební VŠB-TUO</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Advances in Concrete Technology and Sustainability Issues : 12th International Conference on Recent Advances in Concrete Technology and Sustainability Issues held in Prague, Czech Republic, October 30th to November 2, 2012 : supplementary papers

ISBN

978-0-9916737-1-1

ISSN

—

e-ISSN

—

Počet stran výsledku

18

Strana od-do

351-368

Název nakladatele

American Concrete Institute

Místo vydání

Michigan

Místo konání akce

Praha

Datum konání akce

30. 10. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—